1、Designation:D7905/D7905M14Standard Test Method forDetermination of the Mode II Interlaminar FractureToughness of Unidirectional Fiber-Reinforced PolymerMatrix Composites1This standard is issued under the fixed designation D7905/D7905M;the number immediately following the designation indicates theyea
2、r of original adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method describes the determination of themode II in
3、terlaminar fracture toughness,GIIc,of unidirectionalfiber-reinforced polymer matrix composite laminates undermode II shear loading using the end-notched flexure(ENF)test(Fig.1).1.2 This method is limited to use with composites consistingof unidirectional carbon-fiber-and glass-fiber-reinforced lami-
4、nates.This limited scope reflects the experience gained inround robin testing.This test method may prove useful forother types and classes of composite materials;however,certain interferences have been noted(see Section 6).1.3 The values stated in either SI units or inch-pound unitsare to be regarde
5、d separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used independently of the other.Combiningvalues from the two systems may result in non-conformancewith the standard.1.3.1 Within the text the inch-pound units are shown inbrackets.1.4
6、This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents
7、2.1 ASTM Standards:2D792 Test Methods for Density and Specific Gravity(Rela-tive Density)of Plastics by DisplacementD883 Terminology Relating to PlasticsD2584 Test Method for Ignition Loss of Cured ReinforcedResinsD2734 Test Methods for Void Content of Reinforced PlasticsD3171 Test Methods for Const
8、ituent Content of CompositeMaterialsD3878 Terminology for Composite MaterialsD5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer MatrixComposite MaterialsD5687/D5687M Guide for Preparation of Flat CompositePanels with Processing Guidelines for Specimen
9、 Prepara-tionD7264/D7264M Test Method for Flexural Properties ofPolymer Matrix Composite MaterialsE4 Practices for Force Verification of Testing MachinesE6 Terminology Relating to Methods of Mechanical TestingE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE122 Practice for Calculating
10、Sample Size to Estimate,WithSpecified Precision,the Average for a Characteristic of aLot or ProcessE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE456 Terminology Relating to Quality and StatisticsE691 Practice for Conducting an Interlaboratory Study toDetermine the Precisi
11、on of a Test MethodE1309 GuideforIdentificationofFiber-ReinforcedPolymer-Matrix Composite Materials in DatabasesE1434 Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in DatabasesE1471 Guide for Identification of Fibers,Fillers,and CoreMaterials in Computerized Materi
12、al Property Databases3.Terminology3.1 Terminology D3878 defines terms relating to high-modulous fibers and their composites.Terminology D883defines terms relating to plastics.Terminology E6 defines termsrelating to mechanical testing.Terminology E456 and PracticeE177 define terms relating to statist
13、ics.In the event of conflictbetween terms,Terminology D3878 shall have precendenceover the other terminology standards.1This test method is under the jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.06 onInterlaminar Properties.Current edi
14、tion approved Oct.1,2014.Published November 2014.DOI:10.1520/D7905_D7905M-142For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe AST
15、M website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 NOTE1If the term represents a physical quantity,its analyticaldimensions are stated immediately following the term(or letter symbol)infundamental dimension form,using the following
16、 ASTM standard sym-bology for fundamental dimensions,shown within square brackets:Mfor mass,L for length,T for time,u for thermodynamic temperature,and nd for non-dimensional quantities.Use of these symbols is restrictedto analytical dimensions when used with square brackets,as the symbolsmay have other definitions when used without the brackets.3.2 Definitions of Terms Specific to This Standard:3.2.1 Compliance Calibration(CC)Methodthe method ofdata reduction where the relationship between spec