1、Designation:D7078/D7078M201Standard Test Method forShear Properties of Composite Materials by V-Notched RailShear Method1This standard is issued under the fixed designation D7078/D7078M;the number immediately following the designation indicates theyear of original adoption or,in the case of revision
2、,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1NOTEEditorial corrections were made to the adjunct information in March 2021.1.Scope1.1 This test method covers the dete
3、rmination of the shearproperties of high-modulus fiber-reinforced composite materi-als by clamping the ends of a V-notched specimen between twopairs of loading rails.When loaded in tension,the railsintroduce shear forces into the specimen through the specimenfaces.In comparison,the specimen of Test
4、Method D5379/D5379M is loaded through its top and bottom edges.Faceloading allows higher shear forces to be applied to thespecimen,if required.Additionally,the present test methodutilizes a specimen with a larger gage section than theV-notched specimen of Test Method D5379/D5379M.In bothtest methods
5、,the use of a V-notched specimen increases thegage section shear stresses in relation to the shear stresses inthe vicinity of the grips,thus localizing the failure within thegage section while causing the shear stress distribution to bemore uniform than in a specimen without notches.Incomparison,Tes
6、t Method D4255/D4255M utilizes an un-notched specimen clamped between two pairs of loading railsthat are loaded in tension.Also,in contrast to Test MethodD4255/D4255M,the present test method provides specimengripping without the need for holes in the specimen.The composite materials are limited to c
7、ontinuous-fiber ordiscontinuous-fiber-reinforced composites in the following ma-terial forms:1.1.1 Laminates composed only of unidirectional fibrouslaminae,with the fiber direction oriented either parallel orperpendicular to the fixture rails.1.1.2 Laminates of balanced and symmetric construction,wi
8、th the 0 direction oriented either parallel or perpendicular tothe fixture rails.1.1.3 Laminates composed of woven,braided,or knittedfabric filamentary laminae.1.1.4 Short-fiber-reinforced composites with a majority ofthe fibers being randomly distributed.1.2 UnitsThe values stated in either SI unit
9、s or inch-pound units are to be regarded separately as standard.Thevalues stated in each system are not necessarily exact equiva-lents;therefore,to ensure conformance with the standard,eachsystem shall be used independently of the other,and valuesfrom the two systems shall not be combined.1.2.1 With
10、in the text,the inch-pound units are shown inbrackets.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the app
11、licability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by
12、the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D792 Test Methods for Density and Specific Gravity(Rela-tive Density)of Plastics by DisplacementD883 Terminology Relating to PlasticsD2584 Test Method for Ignition Loss of Cured Reinforced
13、ResinsD2734 Test Methods for Void Content of Reinforced PlasticsD3171 Test Methods for Constituent Content of CompositeMaterialsD3878 Terminology for Composite MaterialsD4255/D4255M Test Method for In-Plane Shear Propertiesof Polymer Matrix Composite Materials by the Rail ShearMethod1This test metho
14、d is under the jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.04 onLamina and Laminate Test Methods.Current edition approved April 1,2020.Published April 2020.Originallyapproved in 2005.Last previous edition approved in 2019 as D7078/D70
15、78M 19.DOI:10.1520/D7078_D7078M-20E01.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International
16、,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1D5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer Matri