1、Designation:D658017Standard Test Method forThe Determination of Metallic Zinc Content in Both ZincDust Pigment and in Cured Films of Zinc-Rich Coatings1This standard is issued under the fixed designation D6580;the number immediately following the designation indicates the year oforiginal adoption or
2、,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the determination by differentialscanning calorimetry of the m
3、etallic zinc content of bothzinc-dust pigment,and of dried films of zinc-rich coatings.This test method is applicable to both inorganic and organiczinc-rich coatings1.2 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.3 This st
4、andard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This intern
5、ational standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Commi
6、ttee.2.Referenced Documents2.1 ASTM Standards:2D521 Test Methods for Chemical Analysis of Zinc Dust(Metallic Zinc Powder)E691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method3.Summary of Test Method3.1 Samples of either zinc-dust pigment or of cured films o
7、fzinc-rich coatings are ground in a mortar and pestle,thencarefully weighed into standard differential scanning calorim-etry(DSC)sample pans.The pans are then crimped shut,andanalyzed in a differential scanning calorimeter in a singledynamic heating step,ranging from 370 to 435C at 10C permin,under
8、a nitrogen purge.The percent metallic zinc in thesample is determined by measuring the energy associated withthe endothermic peak near 419C caused by the melting of themetallic zinc,and comparing this value to the heat of fusion ofpure zinc.4.Significance and Use4.1 This test method is useful for de
9、termining the amount ofmetallic zinc in zinc dust pigment,and also in dried films ofboth inorganic and organic zinc-rich coatings.Test MethodsD521 is an appropriate method for analyzing zinc dust,but hasshortcomings when applied to samples of cured coatings.5.Interferences5.1 An increase or decrease
10、 in heating rate from thosespecified may slightly alter the results.However,the variationwould be expected to be minimal,so long as the zinc referencestandard and the samples are subjected to the same heatingrate.5.2 Daily calibration of the calorimeter with high purity zincfoil results in improved
11、results.Reagent grade zinc granules orzinc powder are of insufficient purity to properly calibrate theinstrument.Furthermore,the high purity-zinc foil should onlybe used one time as a calibration standard.WarningUsingthe same piece of foil more than once can result in inaccurateresults,due to oxidat
12、ion of the zinc at the high temperatures inthe calorimeter,coupled with the alloying effects of zinc withthe aluminum sample pans.5.3 Important steps in achieving accurate and reproducibleresults are very gentle tapping of the pan in order to distributethe sample evenly over the bottom of the pan,an
13、d carefulplacement of the pan lid to avoid expulsion of the fine powderduring crimping.NOTE1Round-robin testing has shown no evidence that pyrolysis ofthe binder interferes with the measurement of the heat of fusion.Eitherpyrolysis does not occur,occurs during stabilization of the instrumentprior to
14、 the scan,or is negligible due to the small amount of binder presentin such coatings.If there is reason to suspect interference from the binder,the analyst may wish to test a blank sample of binder(with no zinc1This test method is under the jurisdiction of ASTM Committee D01 on Paintand Related Coat
15、ings,Materials,and Applications and is the direct responsibility ofSubcommittee D01.21 on Chemical Analysis of Paints and Paint Materials.Current edition approved Dec.1,2017.Published January 2018.Originallyapproved in 2000.Last previous edition approved in 2009 as D6580 00(2009).DOI:10.1520/D6580-1
16、7.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Princip