1、Designation:D611597(Reapproved 2019)Standard Test Method forMode I Fatigue Delamination Growth Onset of UnidirectionalFiber-Reinforced Polymer Matrix Composites1This standard is issued under the fixed designation D6115;the number immediately following the designation indicates the year oforiginal ad
2、option or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method determines the number of cycles(N)for the onset of delaminat
3、ion growth based on the openingmode I cyclic strain energy release rate(G),using the DoubleCantilever Beam(DCB)specimen shown in Fig.1.This testmethod applies to constant amplitude,tension-tension fatigueloading of continuous fiber-reinforced composite materials.When this test method is applied to m
4、ultiple specimens atvarious G-levels,the results may be shown as a GN curve,asillustrated in Fig.2.1.2 This test method is limited to use with compositesconsisting of unidirectional carbon fiber tape laminates withsingle-phase polymer matrices.This limited scope reflects theexperience gained in roun
5、d robin testing.This test method mayprove useful for other types and classes of composite materials,however,certain interferences have been noted(see Section 6.5of Test Method D5528).1.3 The values stated in SI units are to be regarded asstandard.No other units of measurement are included in thissta
6、ndard.1.3.1 ExceptionThe values provided in parentheses are forinformation only.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practi
7、ces and deter-mine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and R
8、ecom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D883 Terminology Relating to PlasticsD2584 Test Method for Ignition Loss of Cured ReinforcedResinsD2651 Guide for Preparation of Metal Surfaces forAdhesiveBonding
9、D2734 Test Methods for Void Content of Reinforced PlasticsD3171 Test Methods for Constituent Content of CompositeMaterialsD3878 Terminology for Composite MaterialsD5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer MatrixComposite MaterialsD5528 Test M
10、ethod for Mode I Interlaminar Fracture Tough-ness of Unidirectional Fiber-Reinforced Polymer MatrixCompositesE4 Practices for Force Verification of Testing MachinesE6 Terminology Relating to Methods of Mechanical TestingE122 Practice for Calculating Sample Size to Estimate,WithSpecified Precision,th
11、e Average for a Characteristic of aLot or ProcessE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE456 Terminology Relating to Quality and StatisticsE467 Practice for Verification of Constant Amplitude Dy-namic Forces in an Axial Fatigue Testing SystemE691 Practice for Conduc
12、ting an Interlaboratory Study toDetermine the Precision of a Test MethodE739 Practice for StatisticalAnalysis of Linear or LinearizedStress-Life(S-N)and Strain-Life(-N)Fatigue DataE1049 Practices for Cycle Counting in Fatigue AnalysisE1150 Definitions of Terms Relating to Fatigue(Withdrawn1996)31Thi
13、s test method is under the jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.06 onInterlaminar Properties.Current edition approved March 15,2019.Published March 2019.Originallyapproved in 1997.Last previous edition approved in 2011 as D6115
14、 97(2011).DOI:10.1520/D6115-97R19.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved version of th
15、is historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Dec
16、ision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 3.Terminology3.1 Terminology D3878 defines terms relating to high-modulus fibers and their composites.Terminology D883 de-fines terms relating to plastics.Terminology E6 defines termsrelating to mechanical testing.Terminology E456 and PracticeE177 define terms relating to statistics.Definitions E1150defines terms relating