1、Designation:D470513Standard Test Method forStitch Tear Strength of Leather,Double Hole1This standard is issued under the fixed designation D4705;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in pa
2、rentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method is intended for use in determining thestitch tear
3、ing resistance of leather using a double hole tear.It isparticularly applicable to lightweight leathers.This test methoddoes not apply to wet blue.1.2 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are
4、provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bil
5、ity of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2D1610 Practice for Conditioning Leather and Leather Prod-ucts for TestingD1813 Test Method for Measuring Thickness of LeatherTest SpecimensD2209 Test Method for Tensile Strength of LeatherD2813 Practice for Sampling
6、 Leather for Physical andChemical Tests3.Significance and Use3.1 This test method is designed to measure the loadrequired to tear leather through two holes in the test specimen.Tanners and leather buyers have found that this test gives anindication of the resistance of leather to tearing.It is ofpar
7、ticular value in estimating the durability of leather towithstand tearing stresses encountered in the manufacture ofshoes,garments,and upholstered products.The thickness ofthe specimen and direction of tear relative to the backbone willaffect the uniformity of the test results.This test method mayno
8、t apply when the conditions of the test employed differwidely from those specified in the test method.4.Apparatus4.1 Testing Machine,as described in Test Method D2209.4.2 Thickness Gage,a dead weight type of thickness gage asdescribed in Method D1813.4.3 Steel Die,to cut test specimens(as described
9、in 5.1).4.4 Paper Clip,#1/Premium,with wire diameter 0.041 60.001 in.(1.04 6 0.0254 mm).5.Sampling Test Specimen5.1 Unless otherwise specified,sample the leather accordingto Practice D2813.5.2 The specimen shall be a rectangle of leather 2 in.(50.8mm)in length and 1 in.(25.4 mm)in width with two hol
10、es(564in.(1.98 mm)in diameter on one end of the specimen.Thecenters of the holes shall be14in.(6.35 mm)from the end,14in.(6.35 mm)apart,and located equidistant from the centerline(length wise)of the specimen.See Fig.1.5.3 The specimen shall be cut with the long dimensionperpendicular to the backbone
11、.6.Conditioning6.1 All specimen shall be conditioned and tested in anatmosphere as described in Practice D1610.7.Procedure7.1 Determine the thickness of the specimen to the nearest0.001 in.(0.01 mm)on the long axis near one end.7.2 Bend the wire into a“U”shape,preferably by bendingover a14in.(6.35 m
12、m)rod,and pass the ends through the holesin the specimen so that both ends project from the flesh side ofthe specimen.Clamp both ends of the wire in the testingmachine grip,the jaws of which have been covered.Clamp thefree end of the specimen in the other grip of the testingmachine.1This test method
13、 is under the jurisdiction of ASTM Committee D31 on Leatherand is the direct responsibility of Subcommittee D31.07 on Physical Properties.Current edition approved May 1,2013.Published May 2013.Originallyapproved in 1987.Last previous edition approved in 2012 as D4705-12.DOI:10.1520/D4705-13.2For ref
14、erenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Consho
15、hocken,PA 19428-2959.United States1 7.3 Operate the machine at 10 6 2 in.(254 6 50.8 mm)perminute until the specimen tears.At the instant that thespecimen begins to tear,note and record the load registered bythe machine.8.Report8.1 Report the following:8.1.1 Thickness to the nearest 0.001 in.(0.01 m
16、m)reportedfor each specimen or averaged and reported as the thickness ofthe sample.8.1.2 The tearing strength of the specimen shall be reportedto the nearest 1 lb(0.45 kg).9.Precision and Bias(or Reproducibility)9.1 This test method is adopted from the procedure of theAmerican Leather ChemistsAssociation where it has long beenin use and where it was approved for publication before theinclusion of precision and bias statements was mandated.Theoriginal interlaboratory test data is no longer availa