1、Designation:D490695(Reapproved 2012)Standard Test Method forTotal Solids and Ash Content in Leather Finishing Materials1This standard is issued under the fixed designation D4906;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the yea
2、r of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the total solids and ash contentof finishing materials.1.2 The values stated in SI units are t
3、o be regarded asstandard.No other units of measurement are included in thisstandard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and de
4、termine the applica-bility of regulatory limitations prior to use.2.Significance and Use2.1 This test method is intended for use in determining thetotal solids content and the ash content of a finishing materialbefore its use on any leather.3.Apparatus3.1 Two Tared Platinum Dishes.3.2 Drying Oven,th
5、at operates at 43C 6 3C and 93C 63C.3.3 Desiccator,with calcium chloride or other desiccant.3.4 Muffle Furnace,capable of maintaining temperatures of(600C 6 25C).4.Sampling4.1 One 5-g and one 10-g sample of the finishing materialshall be weighed with accuracy to within 0.001 g.5.Procedure5.1 Total S
6、olids:5.1.1 Place the samples,which have been weighed inplatinum dishes,in the oven for 16 h at 43C followed by 2 hat 93C.(If two ovens at different temperatures are notavailable,increase the temperature in the first oven for the 2-hheating.)5.1.2 Remove the dishes from the oven,place them in adesic
7、cator for 1 h to cool to room temperature and weigh.Return the dishes to the oven for 1 h at 93C and,after coolingin a desiccator for 1 h,weigh again.5.1.3 If the weight loss in the 1-h drying period did notchange the total solids percentage more than 0.1%,report theresults.If greater than 0.1%loss
8、was obtained from the last1-h drying period,then repeat the drying until the change isless than 0.1%.5.2 Ash:5.2.1 Place each platinum dish,containing the residue fromthe total solids determination,in a muffle furnace at 600C 625C for 2 h.5.2.2 If difficulty is encountered in completely burning offt
9、he carbon,leach the residue with hot water(filtering throughashless filter paper)and further ignite this residue in the mufflefurnace.5.2.3 To the dish containing the cooled ash,add the filtrate;evaporate to dryness and heat for 30 min at 600C 6 25C.Theproduct shall then be cooled in a dessicator an
10、d weighed.6.Calculation6.1 The percent total solids of the finishing material shall becalculated as follows:Total solids,percent5AB3100(1)where:A=final weight of solid matter after drying,andB=the original weight of the sample.6.2 The percent ash content of the finishing material shall becalculated
11、as follows:Ash content,percent5CB3100(2)where:C=final weight of ash,andB=the original weight of the sample.1This test method is under the jurisdiction of ASTM Committee D31 on Leatherand is the direct responsibility of Subcommittee D31.06 on Chemical Analysis andhas been produced in cooperation with
12、 the American Leather Chemists Association.(Method K 1-1956).Current edition approved April 1,2012.Published April 2012.Originallyapproved in 1989.Last previous edition approved in 2006 as D490695(2006).DOI:10.1520/D4906-95R12.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Consh
13、ohocken,PA 19428-2959.United States1 7.Report7.1 The total solids in the finishing material is the average ofthe duplicate results and shall be reported in percent.7.2 The ash content of the finishing material,likewise,is theaverage of the duplicate results and shall also be reported inpercent.8.Pre
14、cision and Bias8.1 No justifiable statement can be made on the precisionand bias of this test method because the original interlaboratorytest data is no longer available.8.2 However,the user is cautioned to verify by the use ofreference materials,if available,that the precision and bias ofthis test
15、method is adequate for the contemplated use.9.Keywords9.1 ash;finishes;finishing materials;total solidsASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard.Users of this standard are expressly advised that de
16、termination of the validity of any such patent rights,and the riskof infringement of such rights,are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised,either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters.Your comments will receive careful consid