1、Designation:D57204(Reapproved 2019)Standard Test Method forRubberDeterioration by Heat and Oxygen1This standard is issued under the fixed designation D572;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A nu
2、mber in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method covers a procedure to determine therela
3、tive deterioration resistance of vulcanized rubber in a hightemperature and high pressure oxygen environment.There maybe no exact correlation between this accelerated test andnatural aging of rubber because of the varied conditions ofnatural aging.This accelerated test is suitable for laboratorycomp
4、ound or product comparisons.NOTE1For evaluating rubber vulcanizates under less severe condi-tions more nearly approaching natural aging,the use of Test MethodsD573 and D865 is recommended.1.2 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for info
5、rmationonly.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior
6、 to use.(For specific precautionary statement,see Note 2.)1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations is
7、sued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D15 Method of Compound and Sample Preparation forPhysical Testing of Rubber Products(Withdrawn 1975)3D412 Test Methods for Vulcanized Rubber and Thermoplas-tic ElastomersTensionD45
8、4 Test Method for Rubber Deterioration by Heat andAirPressureD573 Test Method for RubberDeterioration in an AirOvenD865 Test Method for RubberDeterioration by Heating inAir(Test Tube Enclosure)D3182 Practice for RubberMaterials,Equipment,and Pro-cedures for Mixing Standard Compounds and PreparingSta
9、ndard Vulcanized SheetsD3183 Practice for RubberPreparation of Pieces for TestPurposes from ProductsD4483 Practice for Evaluating Precision for Test MethodStandards in the Rubber and Carbon Black ManufacturingIndustries3.Summary of Test Method3.1 Specimens of vulcanized rubber are exposed to a dete-
10、riorating influence at a specified elevated temperature andoxygen pressure for known periods of time,after which theirphysical properties are determined.These are compared withthe properties determined on the original specimens and thechanges noted.3.2 Unless otherwise specified,the determination of
11、 thephysical properties shall be carried out in accordance with TestMethods D412.3.3 Except as may be otherwise specified in this testmethod,the requirements of Practices D3182 and D3183 shallbe complied with and are made part of this test method.3.4 In case of conflict between the provisions of thi
12、s testmethod and those of detailed specifications or test methods fora particular material,the latter shall take precedence.4.Significance and Use4.1 Rubber and rubber products must resist the deteriorationof physical properties with time caused by oxidative andthermal aging.This test method provide
13、s a way to assess theseperformance characteristics of rubber,under certain acceler-ated conditions as specified.1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct responsibility of Subcommittee D11.15on Degradation Tests.Current edi
14、tion approved Nov.1,2019.Published December 2019.Originallyapproved in 1940.Last previous edition approved in 2015 as D572 04(2015).DOI:10.1520/D0572-04R19.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMSta
15、ndards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international
16、 standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 4.2 Please refer to the Annex in Test Method D573 forimportant information on standard compounds used for preci-sion testing for accelerated test aging evaluation.5.Oxygen-Pressure VesselNOTE2Caution:Ad