1、Designation:D5193/D5193M93(Reapproved 2022)Standard Test Method forCoated FabricsAir Retention1This standard is issued under the fixed designation D5193/D5193M;the number immediately following the designation indicates theyear of original adoption or,in the case of revision,the year of last revision
2、.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method describes the determination of theretention of air by fabrics coated on one or both sides withrubber.1.2 The values sta
3、ted in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used independently of the other.Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 This
4、standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This inte
5、rnational standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Com
6、mittee.2.Referenced Documents2.1 ASTM Standards:2D751 Test Methods for Coated Fabrics3.Summary of Test Method3.1 A membrane specimen of the material to be tested isplaced across a circular orifice in the measuring apparatus.Thebottom surface of the membrane is exposed to a source of airat a specifie
7、d pressure.The top surface of the specimen iscovered with water or soap solution.Absence of the appear-ance of air bubbles on the top surface of the material during aspecified exposure period indicates the lack of pin-holes,leaks,or other similar defects.The coated fabric is then acceptable foruse i
8、n the intended application.This procedure is limited tomembranes or coated fabrics having a thickness of less than 3mm 0.125 in.4.Significance and Use4.1 This test method describes a procedure for evaluatingrubberized fabrics that are used to manufacture pneumaticarticles(that is,those that must ret
9、ain air in order to performsatisfactorily in an intended application).Examples of sucharticles are emergency rafts,life preservers,marine recre-ational equipment,floats,pontons,and warning or detectiondevices,such as buoys or weather balloons.5.Apparatus5.1 The test apparatus shall consist of the as
10、sembly shownin Fig.1.5.2 If preferred,wing nuts or toggle clamps may be substi-tuted to facilitate assembly and disassembly of the apparatus,as long as an air-tight seal is maintained during testing.6.Test Conditions6.1 Unless otherwise specified,the standard conditions fortesting coated fabrics as
11、cited in Test Methods D751 shall beused.All specimens and equipment shall be preconditioned for1 h prior to conducting the test.7.Time Lapse Between Vulcanization and Testing7.1 For all purposes,the minimum time between vulcaniza-tion and testing shall be 16 h.7.2 For nonproduct tests,the maximum ti
12、me between vul-canization and testing shall be four weeks,and for evaluationsintended to be comparable,the tests,as far as possible,shouldbe carried out after the same time interval.7.3 For product tests,whenever possible,the time betweenvulcanization and testing should not exceed three months.8.Tes
13、t Specimens8.1 Three circular test specimens,330 6 3 mm 13 6 0.1in.in diameter,shall be accurately cut from the coated fabric.1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct responsibility of Subcommittee D11.37on Coated Fabrics,
14、Rubber Threads and Seals.Current edition approved Oct.1,2022.Published November 2022.Originallyapproved in 1991.Last previous edition approved in 2017 as D5193/D5193M 93(2017).DOI:10.1520/D5193_D5193M-93R22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Se
15、rvice at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accord
16、ance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1Holes conforming to the size and location of the bolts,asshown in Fig.1,shall be punched around the perimeter of eachpiece.NOTE1Specimen size is not critical.An apparatus which canaccommodate specimens having a diameter as small as 254