1、Designation:D357615Standard Test Method forCell Size of Rigid Cellular Plastics1This standard is issued under the fixed designation D3576;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parenthes
2、es indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This test method covers the determination of the appar-ent cell size of rigid cellular plastics by counting the number ofcell-wall intersections in a specifi
3、ed distance.1.2 Procedure A requires the preparation of a thin slice,notmore than one half the average cell diameter in thickness,thatis mechanically stable.For most rigid cellular plastics thislimits the test method to materials with an average cell size ofat least 0.2 mm.1.3 Procedure B is intende
4、d for use with materials whosefriable nature makes it difficult to obtain a thin slice forviewing.1.4 The values stated in SI units are to be regarded asstandard.The values given in parentheses are for informationonly.1.5 This standard does not purport to address all of thesafety concerns,if any,ass
5、ociated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.NOTE1The annex to ISO 2896 is technically equivalent to this testmethod.2.Referenced Documents2.1 AS
6、TM Standards:2D883 Terminology Relating to PlasticsD2842 Test Method for Water Absorption of Rigid CellularPlasticsD6226 Test Method for Open Cell Content of Rigid CellularPlasticsE691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method2.2 ISO Standard:ISO 289
7、6 Cellular Plastics,RigidDetermination of WaterAbsorption33.Terminology3.1 Definitions of terms applicable to this test method aregiven in Terminology D883.4.Summary of Test Method4.1 Procedure AThe cellular plastic specimen is cut to notmore than one half the average cell diameter in thickness on a
8、slicer and the shadowgraph is projected on a screen by the useof a cell-size scale slide assembly and a projector.The averagechord length is obtained by counting the cells on cell-wallintersections and converting this value to average cell size bymathematical derivation.4.2 Procedure BThe cellular p
9、lastic specimen is sliced toprovide a smooth surface.The cell walls are accented by theuse of a marking pen or marking ink.The average chord lengthis obtained by counting the cell wall intersections and convert-ing this value to average cell size by mathematical derivation.5.Significance and Use5.1
10、Several physical properties of rigid cellular plastics aredependent on cell size and cell orientation.Measuring waterabsorption and open-cell content in accordance with TestMethod D2842 and Test Method D6226 requires knowledge ofsurface cell volume,which uses cell size values in thecalculations.5.2
11、This test method provides an apparent cell size becauseit assumes that there is no measurable edge to edge or top tobottom variation in average cell size and that the cell sizedistribution about the average cell size is normal.If the analystis concerned there may be significant variation in either t
12、heaverage cell size or the cell size distribution more detailedanalysis may be required.5.3 Before proceeding with this test method,referenceshould be made to the specification of the material being tested.Any test specimen preparation,conditioning,dimensions,ortesting parameters,or a combination th
13、ereof,covered in the1This test method is under the jurisdiction of ASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.22 on Cellular Materials-Plastics and Elastomers.Current edition approved Oct.1,2015.Published October 2015.Originallyapproved in 1977.Last previous e
14、dition approved in 2010 as D3576-04(2010).DOI:10.1520/D3576-15.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Av
15、ailable from American National Standards Institute(ANSI),25 W.43rd St.,4th Floor,New York,NY 10036,http:/www.ansi.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 materia
16、ls specification shall take precedence over those men-tioned in this test method.If there are no materialspecifications,then the default conditions apply.6.Apparatus6.1 The apparatus required to perform the test as defined byProcedure A is listed as follows:6.1.1 Cell Size Specimen SlicerCutting blade apparatuscapable of slicing thin specimens(0.02 mm)for cell sizeviewing.Fig.1 shows an acceptable alternative slicing appa-ratus.6.1.2 Cell Size ProjectorConventional 35-mm slide pro-jector that ac