1、Designation:D234700(Reapproved 2021)Standard Test Method forMeasuring Area of Leather Test Specimens1This standard is issued under the fixed designation D2347;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.
2、A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the measurement of the surfacearea of leather test specimens.Unless otherwise specified,thesurface to be measured
3、 shall be the grain surface or the surfacemost closely adjacent to the grain surface.This test methoddoes not apply to wet blue.1.2 The values stated in SI units are to be regarded asstandard.No other units of measurement are included in thisstandard.1.3 This standard does not purport to address all
4、 of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in acco
5、r-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM St
6、andards:2D1610 Practice for Conditioning Leather and Leather Prod-ucts for Testing3.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 area of a circular specimenthe average diametersquared and multiplied by4and reported to the nearest 1 mm2.3.1.2 area of a rectangular specimenthe p
7、roduct of theaverage distance across the width of the grain surface multi-plied by the average distance across the length of the grainsurface of the leather specimen to the nearest 1 mm2.4.Significance and Use4.1 This test method is designed to measure the area ofspecimens before and after they are
8、subjected to various teststhat may effect surface area.Two test procedures wherein suchmeasurements could be used are for the apparent density ofleather and the resistance of leather to synthetic perspirationsolution.5.Apparatus5.1 Die,of appropriate size for round or rectangular leatherspecimens,ha
9、ving uniform dimensions in the 50 to 80 mmrange.When rigid and thick leathers,such as sole leathers,arebeing measured,a knife may be used to produce the testspecimen provided straight edges are obtained.5.2 Mallet or Clicking Machine.5.3 Rule or Steel Tape,graduated to 1.0 mm.5.4 Caliper,graduated t
10、o 1.0 mm(recommended for soleleather).6.Test Specimen6.1 The specimen shall be a circular or rectangular piece ofleather cut from leather sides or skins that have been condi-tioned in accordance with Practice D1610 for 48 h in anatmosphere maintained at 73.4 6 1.8 F(23 6 1 C)and 50 64%relative humid
11、ity.6.2 The specimens used in this test method generally rangein area from 1500 to 10 000 mm2.6.3 Do not die out or cut specimens from areas that showsurface defects such as indentations,creases,or cuts.7.Procedure7.1 Place the specimen with the grain side up on a flatsurface and spread it out witho
12、ut pulling or stretching.Using arule or steel tape for flexible leathers and a caliper for soleleathers,make three measurements equally spaced along thewidth and three measurements along the length of the specimento the nearest 1.0 mm.7.2 Measure the diameter of the specimen by placing a ruleor stee
13、l tape across its widest girth and note the length on therule or tape extending over the specimen.Repeat this measure-ment four times at radii approximately 45 to each other andaverage the results to obtain the diameter.1This test method is under the jurisdiction of ASTM Committee D31 on Leatherand
14、is the direct responsibility of Subcommittee D31.07 on Physical Properties.Current edition approved Sept.1,2021.Published October 2021.Originallyapproved in 1965.Last previous edition approved in 2015 as D2347 00(2015).DOI:10.1520/D2347-00R21.2For referenced ASTM standards,visit the ASTM website,www
15、.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis internatio
16、nal standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.18.Calculation and Report8.1 Multiply the average value obtained for the length bythe average value obtained for the width to determine the areaof the specimen.8.2 Calculate the area of circular test s