1、Designation:D417911(Reapproved 2017)Standard Test Method forSingle Pellet Crush Strength of Formed Catalysts andCatalyst Carriers1This standard is issued under the fixed designation D4179;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revisi
2、on,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers determining the resistance offormed catalysts and catalyst carriers to compressive f
3、orce andis applicable to regular catalyst shapes such as tablets andspheres.Extrudates,granular materials,and other irregularshapes are specifically excluded.1.2 This test method determines the average crush strengthin the range from 0 to 50 lbf(0 to 220 N).Some materials mayhave crush strengths abo
4、ve 50 lbf(220N);the test method isapplicable to these materials,but the precision of the test is notknown.1.3 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not
5、considered standard.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitatio
6、ns prior to use.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization Techn
7、icalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2E177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE456 Terminology Relating to Quality and StatisticsE691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method3.
8、Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 pelletsany catalyst shapetablets,spheres,or othersimilar configurationthat is not otherwise excluded from thescope of this test method.3.1.2 tabletstableted cylindrical catalyst particles,eithersolid or hollow core,with lengths that
9、 do not vary from themean by more than 610%.4.Summary of Test Method4.1 Individual pellets taken from a representative sample areplaced between two flat surfaces,subjected to a compressiveload,and the force required to crush the pellet is measured.Theprocedure is replicated and the average of all me
10、asurementstaken is determined.5.Significance and Use5.1 This test method is intended to provide informationconcerning the ability of a catalyst shape to retain physicalintegrity during use.6.Apparatus6.1 A suitable compression testing device is required,con-sisting of the following:6.1.1 Calibrated
11、Gauge,marked for direct reading of theforce in pounds(newtons).Additionally,a suitable system(mechanical,hydraulic,or pneumatic)must be provided so thatthe rate of force application is both uniform and controllablewithin specified limits.6.1.2 Tool Steel Anvils,between which the sample will becrushe
12、d.The faces of the tool steel anvils shall be smooth andfree from recesses or ridges that would interfere with uniformcontact along the major axis of the pellet.When testing tabletsor spheres,the anvils may be of any convenient size or shapeas long as their length and width are greater than the corr
13、e-sponding dimensions of the tablet or pellet being tested(seeFig.1).1This test method is under the jurisdiction of ASTM Committee D32 onCatalysts and is the direct responsibility of Subcommittee D32.02 on Physical-Mechanical Properties.Current edition approved Sept.1,2017.Published September 2017.O
14、riginallyapproved in 1982.Last previous edition approved in 2011 as D417911.DOI:10.1520/D4179-11R17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Documen
15、t Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principle
16、s for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 7.Sampling7.1 A test sample of 50 to 200 individual pieces shall beobtained from larger composites by riffling or splitting inaccordance with STP 447A,3(paragraph 5.12)with the aim ofobtaining a representative sample that represents shape andsize distribution of the larger composite.The size of the sampleshall depend on the precision requir