1、Designation:D 1055 97Used in USDOE-NE StandardsStandard Specifications forFlexible Cellular MaterialsLatex Foam1This standard is issued under the fixed designation D 1055;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of la
2、st revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon(e)indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1.Scope*1.1 These specifications,2including test metho
3、ds,apply toflexible cellular rubber products known as latex foam rubbersbut do not apply to sponge and expanded rubbers.The basematerial used in their manufacture may be natural rubber,reclaimed rubber,synthetic rubber,or rubber-like materials,alone or in combination.1.2 In case of conflict between
4、the provisions of thesegeneral specifications and those of detailed specifications ortest methods for a particular product,the latter shall takeprecedence.Reference to methods for testing cellular rubberproducts should specifically state the particular test or testsdesired.1.3 The values stated in S
5、I units are to be regarded as thestandard.The values in parentheses are for information only.1.4 The following precautionary caveat pertains only to thetest methods portions,Sections 8,16,18,23,26,29,and 31,ofthese specifications:This standard may involve hazardousmaterials,operations,and equipment.
6、This standard does notpurport to address all of the safety concerns,if any,associatedwith its use.It is the responsibility of the user of this standardto establish appropriate safety and health practices anddetermine the applicability of regulatory limitations prior touse.2.Referenced Documents2.1 A
7、STM Standards:D 395 Test Methods for Rubber PropertyCompressionSet3D 454 Test Method for RubberDeterioration by Heat andAir Pressure3D 572 Test Method for RubberDeterioration by Heat andOxygen3D 573 Test Method for RubberDeterioration in an AirOven3D 1056 Specification for Flexible Cellular Material
8、sSponge or Expanded Rubber4D 3182 Practice for RubberMaterials,Equipment,andProcedures for Mixing Standard Compounds and Prepar-ing Standard Vulcanized Sheets3D 3183 Practice for RubberPreparation of Pieces for TestPurposes from Products33.Terminology3.1 Definitions of Terms Specific to This Standar
9、d:3.1.1 flexible cellular rubbera cellular organic polymericmaterial that will not rupture within 60 s when a specimen 200by 25 by 25 mm is bent around a 25-mm diameter mandrel ata uniform rate to produce 1 lap in 5 s in the form of a helix ata temperature between 18 and 29C.3.1.2 rubberthe term rub
10、ber is used to include bothnatural and synthetic types.3.1.3 skinthe smooth surface of the latex foam rubberproduct,formed by contact with the mold or cover plates,isdefined as a natural skin.4.Materials and Manufacture4.1 Latex Foam RubbersThe structure of latex foamrubbers consists of a network of
11、 open or interconnecting cells.Latex foam rubbers are made from rubber latices or liquidrubbers.They are manufactured in sheet,strip,molded,orspecific shapes.Latex foam rubbers shall have a vulcanizedcellular structure with a porous surface.The cells shall beinterconnecting and of a uniform characte
12、r.Latex foam rubbersmay be either cored or solid.Size,shape,and distribution ofcoring shall be at the producers option but subject to theapproval of the purchaser.5.Grades of Latex Foam Rubbers5.1 Latex foam rubbers shall have their grade numbersdesignated by two letters which identify the kind of l
13、atex foamrubber as follows:RCLatex foam rubbers,cored,and1These specifications are under the jurisdiction of ASTM Committee D-20 onPlastics and are the direct responsibility of Subcommittee D20.22 on CellularPlastics.Current edition approved Nov.10,1997.Published April 1998.Originallypublished as D
14、1055 69.Last previous edition D 1055 90.2These specifications together with Specification D 1056 replace the formerTentative Methods of Testing Cellular Rubber Products(D 552 46a T)and theTentative Specifications for Cellular Rubber Products(D 798 46a T),which wereaccordingly discontinued in 1949.3A
15、nnual Book of ASTM Standards,Vol 09.01.4Annual Book of ASTM Standards,Vol 09.02.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959,United States.RULatex foam rubbers,uncored.Digits followin
16、g the letters are used to indicate the degree offirmness,the softer grades being identified with the lowernumbers and the firmer grades with the higher numbers(seeTable 1).5.2 Suffx Letters may be added singly or in combinationafter any grade number to indicate additional requirementsbeyond those specified in Table 1 as basic requirements.Thesignificance of the approved suffix letters is as follows:SIGNIFICANCE OF SUFFIX LETTERSSuffix LettersCWeather ResistanceADLoad DeflectionAEOil ResistanceAN