1、Designation:A109215Standard Specification forSteel Sheet,as Cold-Reduced,for Conversion to AnnealedCold-Rolled Steel Sheet,and Hot Dip Metallic-Coated SteelSheet1This standard is issued under the fixed designation A1092;the number immediately following the designation indicates the year oforiginal a
2、doption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification covers the requirements for as cold-reduced,steel sheet i
3、n coils intended for conversion intocold-rolled steel sheet on continuous annealing lines,andmetallic-coated steel sheet on continuous hot-dip coating lines.1.2 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units
4、 that are provided for information onlyand are not considered standard.2.Referenced Documents2.1 ASTM Standards:A308/A308M Specification for Steel Sheet,Terne(Lead-TinAlloy)Coated by the Hot-Dip ProcessA463/A463M Specification for Steel Sheet,Aluminum-Coated,by the Hot-Dip ProcessA568/A568M Specific
5、ation for Steel,Sheet,Carbon,Structural,and High-Strength,Low-Alloy,Hot-Rolled andCold-Rolled,General Requirements forA653/A653M Specification for Steel Sheet,Zinc-Coated(Galvanized)or Zinc-Iron Alloy-Coated(Galvannealed)by the Hot-Dip ProcessA792/A792M SpecificationforSteelSheet,55%Aluminum-Zinc Al
6、loy-Coated by the Hot-Dip ProcessA875/A875M Specification for Steel Sheet,Zinc-5%Alu-minum Alloy-Coated by the Hot-Dip ProcessA924/A924M Specification for General Requirements forSteel Sheet,Metallic-Coated by the Hot-Dip ProcessA929/A929M Specification for Steel Sheet,Metallic-Coatedby the Hot-Dip
7、Process for Corrugated Steel PipeA1008/A1008M Specification for Steel,Sheet,Cold-Rolled,Carbon,Structural,High-Strength Low-Alloy,High-Strength Low-Alloy with Improved Formability,SolutionHardened,and Bake HardenableA1046/A1046M Specification for Steel Sheet,Zinc-Aluminum-MagnesiumAlloy-Coated by th
8、e Hot-Dip Pro-cessA1063/A1063M Specification for Steel Sheet,Twin-RollCast,Zinc-Coated(Galvanized)by the Hot-Dip ProcessA1079 Specification for Steel Sheet,Complex Phase(CP),Dual Phase(DP)and Transformation Induced Plasticity(TRIP),Zinc-Coated(Galvanized)or Zinc-Iron Alloy-Coated(Galvannealed)by the
9、 Hot-Dip ProcessA1088 Specification for Steel,Sheet,Cold-Rolled,Com-plex Phase(CP),Dual Phase(DP)and TransformationInduced Plasticity(TRIP)3.Terminology3.1 as cold-reduced steel sheet,nan as-rolled productintended for conversion to annealed cold-rolled steel sheetproduct,or hot-dip metallic-coated s
10、teel sheet product.3.1.1 DiscussionAs a result of the high degree of coldreduction as cold-reduced steel sheet exhibits high tensilestrength with very minimal ductility.4.Classification4.1 The material is in a semi-finished form intended forconversion to cold-rolled steel sheet,or hot-dip metallic-c
11、oatedsheet steel whose designations are described in the followingspecifications:4.1.1 A308/A308M Specification for Steel Sheet,Terne(Lead-Tin Alloy)Coated by the Hot-Dip Process,4.1.2 A463/A463MSpecificationforSteelSheet,Aluminum-oated,by the Hot-Dip Process,4.1.3 A653/A653M Specification for Steel
12、 Sheet,Zinc-Coated(Galvanized)or Zinc-Iron Alloy-Coated(Gal-vannealed)by the Hot-Dip Process,4.1.4 A792/A792M Specification for Steel Sheet,55%Aluminum-Zinc Alloy-Coated by the Hot-Dip Process,4.1.5 A875/A875M Specification for Steel Sheet,Zinc-5%Aluminum Alloy-Coated by the Hot-Dip Process,4.1.6 A9
13、29/A929M Specification for Steel Sheet,Metallic-Coated by the Hot-Dip Process for Corrugated Steel Pipe,1This test method is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.19 on Steel Sheet and Strip.Curren
14、t edition approved July 1,2015.Published July 2015.DOI:10.1520/A1092-15Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 4.1.7 A1008/A1008M Specification for Steel,Sheet,Cold-Rolled,Carbon,Structural,High-Strength Low-Alloy,High-Strength Lo
15、w-Alloy with Improved Formability,SolutionHardened,and Bake Hardenable,4.1.8 A1046/A1046M Specification for Steel Sheet,Zinc-Aluminum-Magnesium Alloy-Coated by the Hot-Dip Process,4.1.9 A1063/A1063M Specification for Steel Sheet,Twin-Roll Cast,Zinc-Coated(Galvanized)by the Hot-Dip Process,4.1.10 A10
16、79 Specification for Steel Sheet,Complex Phase(CP),Dual Phase(DP)and Transformation Induced Plasticity(TRIP),Zinc-Coated(Galvanized)or Zinc-Iron Alloy-Coated(Galvannealed)by the Hot-Dip Process,and4.1.11 A1088 Standard Specification for Steel,Sheet,Cold-Rolled,Complex Phase(CP),Dual Phase(DP)and Transfor-mation Induced Plasticity(TRIP).5.Ordering Information5.1 As cold-reduced steel sheet in coils is produced tothickness requirements expressed to 0.001 in.(0.01 mm).Con-sult the producer for the