1、Designation:B79995(Reapproved 2014)Standard Test Method forPorosity in Gold and Palladium Coatings by Sulfurous Acid/Sulfur-Dioxide Vapor1This standard is issued under the fixed designation B799;the number immediately following the designation indicates the year oforiginal adoption or,in the case of
2、 revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers equipment and methods fordetermining the porosity of gold and palladium coati
3、ngs,particularly electrodeposits and clad metals used on electricalcontacts.1.2 This test method is designed to show whether theporosity level is less or greater than some value which byexperience is considered by the user to be acceptable for theintended application.1.3 Avariety of other porosity t
4、esting methods are describedin the literature.2,3Other porosity test methods are B735,B741,B798,and B809.An ASTM Guide to the selection ofporosity tests for electrodeposits and related metallic coatingsis available as Guide B765.1.4 The values stated in SI units are to be regarded asstandard.The val
5、ues given in parentheses are for informationonly.1.5 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety
6、 Data Sheet(MSDS)for this product/materialas provided by the manufacturer,to establish appropriatesafety and health practices,and determine the applicability ofregulatory limitations prior to use.For specific hazards,seeSection 6.2.Referenced Documents2.1 ASTM Standards:4B374 Terminology Relating to
7、 ElectroplatingB542 Terminology Relating to Electrical Contacts and TheirUseB735 Test Method for Porosity in Gold Coatings on MetalSubstrates by Nitric Acid VaporB741 Test Method for Porosity In Gold Coatings On MetalSubstrates By Paper Electrography(Withdrawn 2005)5B765 Guide for Selection of Poros
8、ity and Gross Defect Testsfor Electrodeposits and Related Metallic CoatingsB798 Test Method for Porosity in Gold or Palladium Coat-ings on Metal Substrates by Gel-Bulk ElectrographyB809 Test Method for Porosity in Metallic Coatings byHumid Sulfur Vapor(“Flowers-of-Sulfur”)3.Terminology3.1 Definition
9、sMany terms used in this test method aredefined in Terminology B542 and terms relating to metalliccoatings are defined in Terminology B374.3.2 Definitions of Terms Specific to This Standard:3.2.1 corrosion products,nthose reaction products ema-nating from the pores that protrude from,or are otherwis
10、eattached to,the coating surface after a vapor test exposure.3.2.2 measurement area(or“significant surface”),nthesurface that is examined for the presence of porosity.Thesignificant surfaces or measurement areas of the part to betested shall be indicated on the drawing of the part or byprovision of
11、suitably marked samples.3.2.2.1 DiscussionFor specification purposes,the signifi-cant surfaces or measurement areas are often defined as those1This test method is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.11 on Ele
12、ctrical Contact Test Methods.Current edition approved Oct.1,2014.Published October 2014.Originallyapproved in 1988.Last previous edition approve in 2009 as B799 95(2009).DOI:10.1520/B0799-95R14.2For example see:Nobel,F.J.,Ostrow,B.D.,and Thompson,D.W.,“PorosityTesting of Gold Deposits,”Plating,Vol 5
13、2,1965,p.1001.3Krumbien,S.J.,“Porosity Testing of Contact Platings,”Proceedings,Connec-tors and Interconnection Technology Symposium,Oct.1987,p 47.4For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards vo
14、lume information,refer to the standards Document Summary page onthe ASTM website.5The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 portions of the surface t
15、hat are essential to the serviceability orfunction of the part,such as its contact properties,or which canbe the source of corrosion products or tarnish films thatinterfere with the function of the part.3.2.3 metallic coatings,ninclude platings,claddings,orother metallic layers applied to the substr
16、ate.The coatings cancomprise a single metallic layer or a combination of metalliclayers.3.2.4 porosity,nthe presence of any discontinuity,crack,or hole in the coating that exposes a different underlying metal.3.2.5 underplate,na metallic coating layer between thesubstrate and the topmost layer or layers.The thickness of anunderplate is usually greater that 0.8 m(30 in.).4.Summary of Test Method4.1 The test method employs concentrated sulfurous acid(H2SO3),which emits sulfur dioxide(SO2)gas accor