1、Designation:B53607(Reapproved 2013)Standard Specification forNickel-Iron-Chromium-Silicon Alloys(UNS N08330 andN08332)Plate,Sheet,and Strip1This standard is issued under the fixed designation B536;the number immediately following the designation indicates the year oforiginal adoption or,in the case
2、of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This specification covers nickel-iron-chromium siliconalloys(UNS N08330 and UNS N08332)*plate,shee
3、t,and stripintended for heat resisting applications and general corrosiveservice.1.2 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 T
4、his standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet(MSDS)for this product/materialas provided
5、by the manufacturer,to establish appropriatesafety and health practices,and determine the applicability ofregulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2B899 Terminology Relating to Non-ferrous Metals and Al-loysB906 Specification for General Requirements for Flat-Roll
6、ed Nickel and Nickel Alloys Plate,Sheet,and Strip3.Terminology3.1 Terms shall be defined in accordance with TerminologyB899.4.General Requirements4.1 Material furnished under this specification shall con-form to the requirements of Specification B906 unless other-wise provided herein.In the case of
7、conflict,the requirementsof this specification shall take precedence.5.Material and Manufacture5.1 Annealing TemperatureAlloy UNS N08330 shall beannealed at 1900F(1040C)minimum.Alloy UNS N08332shall be annealed at 2100F(1150C)minimum.6.Chemical Composition6.1 The material shall conform to the requir
8、ements as tochemical composition specified in Table 1.7.Mechanical and Other Properties7.1 The tensile properties of the material at room tempera-ture shall conform to those shown in Table 2.7.2 Grain SizeAnnealed alloy UNS N08332 shall con-form to an average grain size of ASTM No.5 or coarser.There
9、are no grain size requirements for UNS N08330.8.Permissible Variations in Dimensions and Weight8.1 The tolerances and permissible variations provided inAnnex A1,Permissible Variations in Dimensions,Etc.Inch-Pound(SI)Units,of Specification B906 shall apply.9.Keywords9.1 N08330;N08332;plate;sheet;stri
10、p1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Feb.1,2013.Published February 2013.Originallyapproved in 1970.Last previou
11、s edition approved in 2007 as B536 07.DOI:10.1520/B0536-07R13.*New designation established in accordance with ASTM E527 and SAE J1086,Practice for Numbering Metals and Alloys(UNS).2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.Fo
12、r Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 APPENDIX(No
13、nmandatory Information)X1.FINISHESX1.1 ScopeThis appendix lists the finishes in which plate,sheet,and strip are normally supplied.These are subject tochange and the manufacturer should be consulted for the latestinformation available.X1.2 SheetThe various types of finish procurable on sheetproducts
14、are:X1.2.1 No.1 FinishHot-rolled,annealed,and descaled.X1.2.2 No.2D FinishDull,cold-rolled finish.X1.2.3 No.2B FinishBright,cold-rolled finish.X1.2.3.1 Bright-Annealed FinishA bright cold-rolled fin-ish retained by final annealing in a controlled atmospherefurnace.NOTEX1.1Explanation of Finish:No.1P
15、roduced on hand sheet mills by hot rolling to specifiedthicknesses followed by annealing and descaling.Generally used inindustrial applications,such as for heat or corrosion resistance,wheresmoothness and uniformity of finish is not of particular importance.No.2DProduced on either hand sheet mills o
16、r continuous mills bycold rolling to the specified thickness,annealing,and descaling.The dullfinish may result from the descaling or pickling operation or may bedeveloped by a final light cold-rolled pass on dull rolls.The dull finish isfavorable for the retention of lubricants on the surface in deep drawingoperations.This finish is generally used in forming deep drawn articleswhich may be polished after fabrication.No.2BCommonly produced the same as No.2D,except that theannealed and descaled sh