1、Designation:F167418An American National StandardStandard Test Method forJoint Restraint Products for Use with PVC Pipe1This standard is issued under the fixed designation F1674;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year
2、 of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This test method describes a procedure for qualifyingthe performance of joint restraint products for use on PVCpressur
3、e pipe systems by evaluating the effect of the jointrestraint product on the performance characteristics of PVCpipe during cyclic pressure tests and static pressure tests.ThePVC pipe property values referenced in this test method are forthe 12454 compound as described in Specification D1784 anda 4,0
4、00 HDB shall be obtained by categorizing the LTHS inaccordance with Table 1 in Test Method D2837.That includes,but is not limited to,pipe produced in accordance with thefollowing standards:Specifications D1785 and D2241,andAWWA C900.1.2 This test method determines the short-term performanceof a join
5、t restraint product on PVC pipe,which involves thetesting of restrained joint test sections to the minimum burstpressure requirements of the pipe to determine quick burstperformance.1.3 This test method determines the long-term effect of ajoint restraint product on PVC pipe,which involves the testin
6、gof restrained joint test sections to the sustained pressurerequirements of the pipe for a period of 1000 h.1.4 This test method addresses restraint products that arerated at the full pressure capacity of the PVC pipe on whichthey are used.There are joint restraint devices available that arenot rate
7、d at the full pressure capacity of the pipe.While thoseproducts have proven acceptable and useful in the marketplace,this test method does not apply to those products.1.5 This test method determines the performance of a jointrestraint product on PVC pipe subjected to cyclic pressuresurges.The perfor
8、mance is compared to the baseline perfor-mance of pipe without joint restraint products established byHerbert W.Vinson.21.6 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are provided for information on
9、lyand are not considered standard.1.7 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regula
10、tory limitations prior to use.1.8 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Orga
11、nization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:3D1784 Specification for Rigid Poly(Vinyl Chloride)(PVC)Compounds and Chlorinated Poly(Vinyl Chloride)(CPVC)CompoundsD1785 Specification for Poly(Vinyl Chloride)(PVC)PlasticPipe,Schedules 40,80,and 120D2241 Sp
12、ecification for Poly(Vinyl Chloride)(PVC)Pressure-Rated Pipe(SDR Series)D2837 Test Method for Obtaining Hydrostatic Design Basisfor Thermoplastic Pipe Materials or Pressure Design Basisfor Thermoplastic Pipe ProductsF412 Terminology Relating to Plastic Piping Systems2.2 AWWA Standards:AWWA C900 Poly
13、vinyl Chloride(PVC)Pressure Pipe andFabricated Fittings,4 in.through 12 in.(100 mm through300 mm),for Water Distribution43.Terminology3.1 DefinitionsDefinitions are in accordance with Termi-nology F412 unless otherwise specified.1This test method is under the jurisdiction of ASTM Committee F17 on Pl
14、asticPiping Systems and is the direct responsibility of Subcommittee F17.20 on Joining.Current edition approved Nov.1,2018.Published December 2018.Originallyapproved in 1996.Last previous edition approved in 2011 as F167411.DOI:10.1520/F1674-18.2Vinson,Herbert W.,Response of PVC Pipe to Large,Repeti
15、tive PressureSurges,International Conference on Underground Plastic Pipe,American Societyof Civil Engineers,New York,NY,1981,p.491.3For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information
16、,refer to the standards Document Summary page onthe ASTM website.4Available from American Water Works Association(AWWA),6666 W.QuincyAve.,Denver,CO 80235,http:/www.awwa.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Princ