1、Designation:E102/E102M93(Reapproved 2016)Standard Test Method forSaybolt Furol Viscosity of Bituminous Materials at HighTemperatures1This standard is issued under the fixed designation E102/E102M;the number immediately following the designation indicates the yearof original adoption or,in the case o
2、f revision,the year of last revision.A number in parentheses indicates the year of last reapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the empirical procedures fordetermining the Saybolt Furol viscosities of bi
3、tuminous mate-rials at specified temperatures between 120 and 240C 248and 464F.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used independently of the ot
4、her.Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices an
5、d determine the applica-bility of regulatory limitations prior to use.See 8.1.2.Referenced Documents2.1 ASTM Standards:2D88 Test Method for Saybolt ViscosityD92 Test Method for Flash and Fire Points by ClevelandOpen Cup TesterD140/D140M Practice for Sampling Bituminous MaterialsE1 Specification for
6、ASTM Liquid-in-Glass ThermometersE11 Specification for Woven Wire Test Sieve Cloth and TestSieves3.Terminology3.1 Definitions:3.1.1 Furolan acronym of“Fuel and road oils.”3.1.2 Saybolt Furol viscositythe corrected efflux time inseconds of 60 mL of sample flowing through a calibrated Furolorifice und
7、er specified conditions.The viscosity value isreported in Saybolt Furol seconds,abbreviated SFS,at aspecified temperature.4.Summary of Test Method4.1 The efflux time in seconds of 60 mL of sample,flowingthrough a calibrated orifice,is measured under carefullycontrolled conditions.The time is correct
8、ed by an orifice factorand reported as the viscosity of the sample at that temperature.5.Significance and Use5.1 This test method is useful in characterizing certainbituminous materials,as one element in establishing unifor-mity of shipments and sources of supply.5.2 This test method is an extension
9、 of Test Method D88.6.Apparatus6.1 Saybolt Furol Viscometer and Bath,as shown anddescribed in Test Method D88,Fig.1 andAnnex 1.An externalheater may also be used,but if so,it shall be more than 51 mm2 in.from the viscometer.An aluminum-block,constant-temperature bath is also acceptable,and no stirri
10、ng device isrequired with this type of bath.6.2 Displacement Ring,as shown in Fig.1,constructed ofthe same corrosion-resistant metal as the viscometer.6.3 CoverA metal cover for the viscometer,cylindricalwith a flat top,approximately 57 mm 214in.in diameter and7 mm 14in.deep(Note 1).One hole slightl
11、y larger than thediameter of a viscosity thermometer shall be drilled in thecenter of the cover,and two smaller holes to permit the verticalrods of the displacement ring to pass through the cover.NOTE1The cover of a 90-mL 3-oz Gill-style ointment box fulfillsthese requirements.6.4 Thermometer Suppor
12、t,as shown in Test Method D88,Fig.3.6.5 Saybolt Viscosity Thermometers,as listed in Table 1,forreading the temperature of the sample.Each thermometer shallconform to the requirements listed in Specification E1 for thatASTM Thermometer Number.1This test method is under the jurisdiction ofASTM Committ
13、ee D08 on Roofingand Waterproofing and is the direct responsibility of Subcommittee D08.05 onSolvent-Bearing Bituminous Compounds for Roofing and Waterproofing.Current edition approved May 1,2016.Published May 2016.Originallyapproved in 1954.Last previous edition approved in 2009 as E102/E102M 93(20
14、09).DOI:10.1520/E0102_E0102M-93R16.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,10
15、0 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 6.6 Bath ThermometersSaybolt Viscosity thermometers,or any other temperature-indicating means of equivalent accu-racy.6.7 Sieve,850-m No.20,conforming to the requirementsof Specification E11.6.8 Receiving Flask,as shown i
16、n Test Method D88,Fig.5.6.9 Timer,graduated in fifths or tenths of a second,andaccurate to within 0.1%when tested over a 60-min interval.Electric timers are acceptable if operated on a controlledfrequency circuit.6.10 Hot Plate,electric,approximately 200 mm 8 in.indiameter,with a three-heat switch,rated at 1200 W at the highheat setting and 500 to 600 W at the medium heat setting.7.Sampling7.1 Sample the material in accordance with Practice D140/D140M.8.Preparation of Apparatus8.1 Clean the visc