1、Designation:E209218aStandard Test Method forDistortion Temperature in Three-Point Bending byThermomechanical Analysis1This standard is issued under the fixed designation E2092;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year
2、of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This test method describes the determination of thetemperature at which the specific modulus of a test specimen isreali
3、zed by deflection in three-point bending.This temperatureis identified as the distortion temperature.The distortiontemperature is that temperature at which a test specimen ofdefined geometry deforms to a level of strain under appliedstress of 0.455 MPa(66 psi)(Method A)and 1.82 MPa(264psi)(Method B)
4、equivalent to those used in Test Method D648.The test is applicable over the range of temperature fromambient to 300 C.NOTE1This test method is intended to provide results similar to thoseof Test Method D648 but is performed on a thermomechanical analyzerusing a smaller test specimen.Equivalence of
5、results to those obtained byTest Method D648 has been demonstrated on a limited number ofmaterials.The results of this test method shall be considered to beindependent and unrelated to those of Test Method D648 unless the userdemonstrates equivalence.1.2 The values stated in SI units are to be regar
6、ded asstandard.No other units of measurement are included in thisstandard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices an
7、d deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-m
8、endations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D648 Test Method for Deflection Temperature of PlasticsUnder Flexural Load in the Edgewise PositionE473 Terminology Relating to Thermal Analysis and Rhe-ologyE1142 Term
9、inology Relating to Thermophysical PropertiesE1363 Test Method for Temperature Calibration of Thermo-mechanical AnalyzersE2113 Test Method for Length Change Calibration of Ther-momechanical AnalyzersE2206 Test Method for Force Calibration of Thermome-chanical Analyzers3.Terminology3.1 DefinitionsSpe
10、cific technical terms used in this stan-dard are defined in Terminologies E473 and E1142,includingstress,strain,and thermomechanical analyzer.3.1.1 distortion temperature C,nthe temperature atwhich an arbitrary strain level is obtained in three-pointbending under an arbitrary load.4.Summary of Test
11、Method4.1 A test specimen of known dimensions is tested inthree-point bending mode.A known stress is applied to thecenter of a test specimen supported near its ends,as it is heatedat a constant rate from ambient temperature to the uppertemperature limit for the material.The deflection of the testspe
12、cimen is recorded as a function of temperature.Thetemperature at which a predetermined level of strain is ob-served in the test specimen is analyzed as the distortiontemperature.1This test method is under the jurisdiction of Committee E37 on ThermalMeasurements and is the direct responsibility of Su
13、bcommittee E37.10 onFundamental,Statistical and Mechanical Properties.Current edition approved Dec.1,2018.Published January 2019.Originallyapproved in 2000.Last previous edition approved in 2018 as E2092 18.DOI:10.1520/E2092-18A.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orco
14、ntact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandardsvolume information,refer tot he standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Consh
15、ohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organi
16、zation Technical Barriers to Trade(TBT)Committee.1 5.Significance and Use5.1 Data obtained by this test method shall not be used topredict the behavior of materials at elevated temperaturesexcept in applications in which the conditions of time,temperature,method of loading,and stress are similar to thosespecified in the test.5.2 This standard is particularly suited for quality controland development work.The data are not intended for use indesign or predicting endurance at elevated temperatures.