1、Designation:D7291/D7291M15Standard Test Method forThrough-Thickness“Flatwise”Tensile Strength and ElasticModulus of a Fiber-Reinforced Polymer Matrix CompositeMaterial1This standard is issued under the fixed designation D7291/D7291M;the number immediately following the designation indicates theyear
2、of original adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method determines the through-thickness“flat-wise”ten
3、sion strength and elastic modulus of fiber reinforcedpolymer matrix composite materials.A tensile force is appliednormal to the plane of the composite laminate using adhesivelybonded thick metal end-tabs.The composite material forms arelimited to continuous-fiber or discontinuous fiber(tape or2-dime
4、nsional fabric,or both)reinforced composites.1.2 The through-thickness strength results using this testmethod will in general not be comparable to Test MethodD6415 since this method subjects a relatively large volume ofmaterial to an almost uniform stress field while Test MethodD6415 subjects a smal
5、l volume of material to a non-uniformstress field.1.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.Within the text,theinch-pound units are shown in brackets.The values stated ineach system are not exact equivalents;therefore,each systemmust be use
6、d independently of the other.Combining valuesfrom the two systems may result in nonconformance with thestandard.1.4 This standard does not purport to address all of thesafety problems,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety
7、 and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2D792 Test Methods for Density and Specific Gravity(Rela-tive Density)of Plastics by DisplacementD883 Terminology Relating to PlasticsD3171 Test Methods for Constitu
8、ent Content of CompositeMaterialsD3878 Terminology for Composite MaterialsD5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer MatrixComposite MaterialsD5687/D5687M Guide for Preparation of Flat CompositePanels with Processing Guidelines for Specimen Pr
9、epara-tionD6415 Test Method for Measuring the Curved BeamStrength of a Fiber-Reinforced Polymer-Matrix Compos-iteE4 Practices for Force Verification of Testing MachinesE6 Terminology Relating to Methods of Mechanical TestingE122 Practice for Calculating Sample Size to Estimate,WithSpecified Precisio
10、n,the Average for a Characteristic of aLot or ProcessE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE251 Test Methods for Performance Characteristics of Me-tallic Bonded Resistance Strain GagesE456 Terminology Relating to Quality and StatisticsE691 Practice for Conducting a
11、n Interlaboratory Study toDetermine the Precision of a Test MethodE1012 Practice for Verification of Testing Frame and Speci-men Alignment Under Tensile and Compressive AxialForce ApplicationE1309 GuideforIdentificationofFiber-ReinforcedPolymer-Matrix Composite Materials in Databases(With-drawn 2015
12、)3E1434 Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in Databases(Withdrawn2015)3E1471 Guide for Identification of Fibers,Fillers,and CoreMaterials in Computerized Material Property Databases(Withdrawn 2015)31This test method is under the jurisdiction of ASTM Comm
13、ittee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.06 onInterlaminar Properties.Current edition approved Oct.1,2015.Published November 2015.Originallyapproved in 2007.Last previous edition approved in 2007 as D7291/D7291M-07.DOI:10.1520/D7291_D7291M-15.2For referenc
14、ed ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm
15、.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 3.Terminology3.1 DefinitionsTerminology D3878 defines terms relatingto high-modulus fibers and their composites.TerminologyD883 defines terms relating to plastics.Terminology E6 defines
16、terms relating to mechanical testing.Terminology E456 andPractice E177 define terms relating to statistics.In the event ofa conflict between terms,Terminology D3878 shall haveprecedence over the other terminologies.NOTE1If the term represents a physical quantity,its analyticaldimensions are stated immediately following the term(or letter symbol)infundamental dimension form,using the following ASTM standard sym-bology for fundamental dimensions,shown within square brackets:Mfor mass,L for length,