1、Designation:D7205/D7205M06(Reapproved 2011)Standard Test Method forTensile Properties of Fiber Reinforced Polymer MatrixComposite Bars1This standard is issued under the fixed designation D7205/D7205M;the number immediately following the designation indicates theyear of original adoption or,in the ca
2、se of revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method determines the quasi-static longitudinaltensile strength and elongation propert
3、ies of fiber reinforcedpolymer matrix(FRP)composite bars commonly used astensile elements in reinforced,prestressed,or post-tensionedconcrete.NOTE1Additional procedures for determining tensile properties ofpolymer matrix composites may be found in test methods D3039/D3039Mand D3916.1.2 Linear elemen
4、ts used for reinforcing Portland cementconcrete are referred to as bars,rebar,rods,or tendons,depending on the specific application.This test method isapplicable to all such reinforcements within the limitationsnoted in the method.The test articles are referred to as bars inthis test method.In gener
5、al,bars have solid cross-sections anda regular pattern of surface undulations and/or a coating ofbonded particles that promote mechanical interlock betweenthe bar and concrete.The test method is also appropriate foruse with linear segments cut from a grid.Specific details forpreparing and testing of
6、 bars and grids are provided.In somecases,anchors may be necessary to prevent grip-induceddamage to the ends of the bar or grid.Recommended details forthe anchors are provided in Annex A1.1.3 The strength values provided by this method are short-term static strengths that do not account for sustaine
7、d static orfatigue loading.Additional material characterization may berequired,especially for bars that are to be used under highlevels of sustained or repeated loading.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach syst
8、em may not be exact equivalents;therefore,eachsystem shall be used independently of the other.Combiningvalues from the two systems may result in non-conformancewith the standard.1.4.1 Within the text,the inch-pound units are shown inbrackets.1.5 This standard does not purport to address all of thesa
9、fety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2A615/A615M Specification for Defor
10、med and Plain Carbon-Steel Bars for Concrete ReinforcementD792 Test Methods for Density and Specific Gravity(Rela-tive Density)of Plastics by DisplacementD883 Terminology Relating to PlasticsD3039/D3039M Test Method for Tensile Properties of Poly-mer Matrix Composite MaterialsD3171 Test Methods for
11、Constituent Content of CompositeMaterialsD3878 Terminology for Composite MaterialsD3916 Test Method for Tensile Properties of PultrudedGlass-Fiber-Reinforced Plastic RodD5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer MatrixComposite MaterialsE4 Pra
12、ctices for Force Verification of Testing MachinesE6 Terminology Relating to Methods of Mechanical TestingE83 Practice for Verification and Classification of Exten-someter SystemsE122 Practice for Calculating Sample Size to Estimate,WithSpecified Precision,the Average for a Characteristic of aLot or
13、ProcessE456 Terminology Relating to Quality and StatisticsE1012 Practice for Verification of Testing Frame and Speci-men Alignment Under Tensile and Compressive AxialForce ApplicationE1309 GuideforIdentificationofFiber-Reinforced1This test method is under the jurisidiction of ASTM Committee D30 onCo
14、mposite Materials and is the direct responsibility of Subcommittee D30.10 onComposites for Civil Structures.Current edition approved Aug.1,2011.Published December 2011.Originallyapproved in 2006.Last previous edition approved in 2006 as D7205/D7205M06.DOI:10.1520/D7205_D7205M-06R11.2For referenced A
15、STM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA
16、 19428-2959.United States1 Polymer-Matrix Composite Materials in DatabasesE1434 Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in DatabasesE1471 Guide for Identification of Fibers,Fillers,and CoreMaterials in Computerized Material Property Databases3.Terminology3.1 Terminology in D3878 defines terms relating to high-modulus fibers and their composites.Terminology in D883defines terms relating to plastics.Terminology in E6 definesterms relating to mechanical test