1、Designation:D772318Standard Test Method forRubber PropertyMacro-Dispersion of Fillers inCompounds1This standard is issued under the fixed designation D7723;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A n

2、umber in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers a procedure to measure themacro-dispersion of fillers in a rubber matrix by quantifyingthe surface roughness of a fr

3、eshly cut specimen using anoptical microscope in reflection mode.1.2 The method provides a procedure to measure the qualityof mixing of reinforcing fillers such as silica and carbon black,as well as inert fillers such as chalk,clay and other solids.1.3 The method includes a sample preparation proced

4、ure forfilled uncured rubber compounds as well as filled cured rubbercompounds.1.4 The values stated in SI units are to be regarded asstandard.No other units of measurement are included in thisstandard.1.5 This standard does not purport to address all of thesafety concerns,if any,associated with its

5、 use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.6 This international standard was developed in accor-dance with internationally recognized principle

6、s on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D2663 Test Methods for Carbon BlackDispe

7、rsion in Rub-berD3053 Terminology Relating to Carbon Black3.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 agglomerates,nany number of filler aggregates heldtogether by van der Waals Forces(carbon black)or hydrogenbonding(silica).3.1.2 macro dispersion,ndegree of distribution of

8、 fillerinto a compound,generally on a scale of less than 100 m butgreater than 2 m;represents micron range agglomeration.3.1.3 nodges,nbumps in a cut surface caused by filleragglomerates in a rubber matrix.3.1.4 surface roughness,nthe bumps(nodges),or hillsand valleys that are on the visible side of

9、 a sample.3.1.5 white area,nthe portion of the scan area whichcontains nodges,or other surface defects;it is described here aswhite,because the reflected light from these surface defects iswhite.4.Summary of Test Method4.1 This standard uses mathematical algorithms to quantifythe surface roughness o

10、f freshly cut rubber specimens asmeasured by a reflected light optical method in two dimen-sions.4.2 The reflected light optical method,generally used todetermine a comparative dispersion rating,is expanded to givequantitative data as to the size and number of nodges.Nodgesdo not show the actual siz

11、e of filler agglomerates.It is assumedthat as the sample is cut,large agglomerates are pushed to oneside or the other leaving a contoured surface.The diameter andfrequency of the surface contours are measured using imageprocessing.These contours are referred to as“nodges”todifferentiate them from ac

12、tual agglomerates.This data ispresented in histogram form of count versus nodge diameter,and allows calculating a measure of dispersion.5.Significance and Use5.1 The incorporation of fillers into the rubber matrix ischaracterized by their macrodispersion as an indicator of thequality of mixing.This

13、test method provides a measure of themacro-dispersion of reinforcing fillers,like silica and carbonblack,as well as of inert fillers.Based on their polymer nature,1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct responsibility of

14、Subcommittee D11.12on Processability Tests.Current edition approved Nov.1,2018.Published November 2018.Originallyapproved in 2011.Last previous edition approved in 2017 as D7723 17.DOI:10.1520/D7723-18.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service

15、 at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance

16、with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 different types of rubbers can show a different degree ofacceptance for the incorporation of fillers,as indicated by theirmacro-dispersion.5.2 Macro-dispersion of carbon black and silica in rubbercompounds may be measured by different metho