1、Designation:D636599(Reapproved 2018)Standard Practice forNondestructive Testing of Geomembrane Seams Using theSpark Test1This standard is issued under the fixed designation D6365;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the ye
2、ar of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This practice covers the nondestructive testing of fieldseams in geomembranes using the spark test.A suspect area isi
3、ndicated by the generation of a spark.The test is applicable toseams made by the extrusion method,seams made by usingwelding tape(a strip of the same type of material as thegeomembrane,that is welded over adjacent sections ofgeomembrane to create a seam),or seams where it is practicalto insert a con
4、ductive material in the seam just prior to orduring fabrication.1.2 The spark test may produce an electrical spark andtherefore can only be used where an electrical spark would notcreate a hazard.1.3 Unless the voltages and distances prescribed are care-fully adhered to,a“false positive”indication m
5、ay result.Thisfalse positive occurs when the arc distance is too large for thevoltage applied at the time and conditions of testing.1.4 The values stated in SI units are to be regarded asstandard.The values given in parentheses are for informationonly.1.5 This standard does not purport to address al
6、l of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.6 This international standard was developed in acc
7、or-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM S
8、tandards:2D4439 Terminology for GeosyntheticsD4491/D4491M Test Methods for Water Permeability ofGeotextiles by Permittivity3.Terminology3.1 Definitions:3.1.1 geomembrane,nan essentially impermeable geosyn-thetic composed of one or more synthetic sheets.3.1.1.1 DiscussionIn geotechnical engineering,“
9、essen-tially impermeable”means that no measurable liquid flowsthrough a geosynthetic when tested in accordance with TestMethods D4491/D4491M.3.1.2 seam,na permanent joining of two or more materi-als.3.2 For definitions of other terms,see Terminology D4439.4.Summary of Practice4.1 To use this practic
10、e,a conductive material is insertedinto the field seam just prior to or during fabrication.Theconductive material in the seam is connected to the negativeterminal of the test apparatus,and a positive voltage is appliedacross the seam edge.Asuspect area in the seam is indicated bya spark from the vol
11、tage source to the conductive material.5.Significance and Use5.1 Spark testing of geomembrane field seams is particu-larly useful in locations where other nondestructive test meth-ods are not practical,for example in tight corners or acircumferential seam around a pipe.6.Apparatus6.1 The test appara
12、tus consists of a high-voltage,low-current source with a negative terminal for ground and a1This practice is under the jurisdiction of ASTM Committee D35 on Geosyn-thetics and is the direct responsibility of Subcommittee D35.10 on Geomembranes.Current edition approved Feb.1,2018.Published February 2
13、018.Originallyapproved in 1999.Last previous edition approved in 2011 as D6365 99(2011).DOI:10.1520/D6365-99R18.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the stand
14、ards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision
15、on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 positive terminal for a voltage applicator.A voltage applicatormay consist of a handle and wire brush,conductive neoprenesqueegee,
16、or other suitable applicator.6.2 The range of the high voltage source is typically 20 000to 35 000 V.6.2.1 The voltage required to cause a discharge(spark)between the positive electrode and the negative electrode wireis expressed by the formula:V 5 K=D(1)where:V=test voltage,K=a constant(V/(mm)1/2),andD=the distance from the edge of the extrusion bead on thelower panel to the conductive material,in mm.6.2.2 If the voltage is not adequate due to underestimatingD,a false positive test(a seam with