1、Designation:D6382/D6382M99(Reapproved 2011)1Standard Practice forDynamic Mechanical Analysis and Thermogravimetry ofRoofing and Waterproofing Membrane Material1This standard is issued under the fixed designation D6382/D6382M;the number immediately following the designation indicates theyear of origi
2、nal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1NOTEUnits information was editorially revised in February 2011.1.Scope1.1 This pr
3、actice covers test procedures and conditions thatare applicable when Test Methods D5023,D5024,D5026,D5279,and D5418 are used for conducting dynamic mechani-cal analysis of roofing and waterproofing membrane material inthree-point bending,compression,tension,torsion,and dualcantilever modes,respectiv
4、ely.The specific method is selectedby the analyst and depends on the membrane material and theoperating principles of the individual instrument used for theanalysis.1.2 This practice covers test procedures and conditions thatare applicable when Test Method E1131 is used for conductingthermogravimetr
5、y of roofing and waterproofing membranematerial.1.3 Membrane materials include bituminous built-up roof-ing,polymer-modified bitumen sheets,vulcanized rubbers,non-vulcanized polymeric sheets,and thermoplastics.Themembrane materials can be either nonreinforced or reinforced.1.4 This practice is appli
6、cable to new membrane materialsreceived from the supplier,those exposed artificially in thelaboratory or outdoors on an exposure rack,and those sampledfrom field installations.1.5 This practice contains notes which are explanatory andare not part of the mandatory requirements of this practice.1.6 Th
7、e values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used independently of the other.Combiningvalues from the two systems may result in non-conformancewith the standa
8、rd.1.7 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Do
9、cuments2.1 ASTM Standards:2D1079 Terminology Relating to Roofing and WaterproofingD4092 Terminology for Plastics:Dynamic MechanicalPropertiesD5023 Test Method for Plastics:Dynamic Mechanical Prop-erties:In Flexure(Three-Point Bending)D5024 Test Method for Plastics:Dynamic Mechanical Prop-erties:In C
10、ompressionD5026 Test Method for Plastics:Dynamic Mechanical Prop-erties:In TensionD5279 Test Method for Plastics:Dynamic Mechanical Prop-erties:In TorsionD5418 Test Method for Plastics:Dynamic Mechanical Prop-erties:In Flexure(Dual Cantilever Beam)E473 Terminology Relating to Thermal Analysis and Rh
11、e-ologyE1131 Test Method for Compositional Analysis by Thermo-gravimetryE1142 Terminology Relating to Thermophysical Properties3.Terminology3.1 DefinitionsFor definitions of terms used in this prac-tice,refer to Terminologies E473,D1079,D4092,and E1142.4.Summary of Practice4.1 In conducting a dynami
12、c mechanical analysis,the roof-ing or waterproofing membrane specimen is placed in a testchamber and subjected to a controlled,increasing temperatureprogram.The temperature range can be from well-below(forexample,80C)to somewhat(for example,50C)above1This practice is under the jurisdiction ofASTM Co
13、mmittee D08 on Roofing andWaterproofing and is the direct responsibility of Subcommittee D08.20 on RoofingMembrane Systems.Current edition approved Jan.1,2011.Published February 2011.Originallyapproved in 1999.Last previous edition approved in 2005 as D6382 99(2005).DOI:10.1520/D6382_D6382M-99R11E01
14、.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,We
15、st Conshohocken,PA 19428-2959.United States1 room temperature.The glass transition temperature,storagemodulus,loss modulus,and damping factor of the specimenare measured.4.2 In conducting a thermogravimetry analysis,the roofingor waterproofing membrane specimen is placed in a testchamber and subject
16、ed to a controlled,increasing temperatureprogram.The temperature range can be from about roomtemperature(for example,20 to 40C)to well-above roomtemperature(for example,900C),and the atmosphere of thechamber is controlled through the use of inert gas such asnitrogen or reactive gas such as air.The percent mass loss ofthe specimen is determined as a function of temperature.5.Significance and Use5.1 Dynamic mechanical analysis provides a measure of therheological properties of roofing and waterpro