1、Designation:D90398(Reapproved 2017)Standard Test Method forPeel or Stripping Strength of Adhesive Bonds1This standard is issued under the fixed designation D903;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revisio
2、n.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method covers the determination of the c
3、om-parative peel or stripping characteristics of adhesive bondswhen tested on standard-sized specimens and under definedconditions of pretreatment,temperature,and testing machinespeed.1.2 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informat
4、iononly.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to
5、use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers
6、 to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D907 Terminology of Adhesives3.Terminology3.1 DefinitionsMany terms used in this test method aredefined in Terminology D907.3.2 Definitions of Terms Specific to This Standard:3.2.1 flexible,nin this test method,indicates a material of
7、the proper flexural strength and thickness to permit a turn backat an approximate 180 angle in the expected loading range ofthe test without failure.In order to fulfill all terms of thedefinition,at least one of the adhered materials must beflexible.3.2.2 peel or stripping strength,nthe average load
8、 per unitwidth of bond line required to separate progressively onemember from the other over the adhered surfaces at a separa-tion angle of approximately 180 and at a separation rate of 152mm(6 in.)/min.It is expressed in kilograms per millimetre(pounds per inch)of width.4.Apparatus4.1 Testing Machi
9、neA power-driven machine,with a con-stant rate-of-jaw separation or of the inclination balance orpendulum type,which fulfills the following requirements:4.1.1 The applied tension as measured and recorded isaccurate within 61%.4.1.2 Hold specimens in the testing machine by grips whichclamp firmly and
10、 prevent slipping at all times.4.1.3 The rate of travel of the power-actuated grip is 305mm(12 in.)/min.This rate which provides a separation of 152mm(6 in.)/min is to be uniform throughout the tests.4.1.4 Operate the machine without any device for maintain-ing maximum load indication.In pendulum-ty
11、pe machines,theweight lever swings as a free pendulum without engagement ofpawls.4.1.5 The machine is autographic giving a chart having theinches of separation as one axis and applied tension as the otheraxis of coordinates.4.1.6 The capacity of the machine is such that the maximumapplied tension du
12、ring test does not exceed 85%nor be lessthan 15%of the rated capacity.4.2 Conditioning Room or DesiccatorsA conditioningroom capable of maintaining a relative humidity of 50 6 2%at 23 6 1C(73.4 6 2F),or desiccators filled with a saturatedsalt solution(Note 1)to give a relative humidity of 50 6 2%at
13、23 6 1C are required for the conditioning of somespecimens.NOTE1A saturated salt solution of calcium nitrate gives approxi-mately 51%relative humidity at the testing temperature.1This test method is under the jurisdiction of ASTM Committee D14 onAdhesives and is the direct responsibility of Subcommi
14、ttee D14.80 on MetalBonding Adhesives.Current edition approved Nov.1,2017.Published November 2017.Originallyapproved in 1946.Last previous edition approved in 2010 as D903 98(2010).DOI:10.1520/D0903-98R17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Serv
15、ice at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordan
16、ce with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 5.Test Specimen5.1 The test specimen,shown in Fig.1(a),consists of onepiece of flexible material,25 by 304.8 mm(1 by 12 in.),bonded for 152.4 mm(6 in.)at one end to one piece of flexibleor rigid material,25 by 203.2 mm(1 by 8 in.),with t