1、Designation:D8066/D8066M17Standard PracticeUnnotched Compression Testing of Polymer MatrixComposite Laminates1This standard is issued under the fixed designation D8066/D8066M;the number immediately following the designation indicates theyear of original adoption or,in the case of revision,the year o
2、f last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This practice provides instructions for using the TestMethod D6484 open hole compression test fixture to determineunnotch
3、ed compressive strength of multi-directional laminates.The composite material forms are limited to continuous-fiberreinforced polymer matrix composites in which the laminate isboth symmetric and balanced with respect to the test direction.The range of acceptable test laminates and thicknesses aredes
4、cribed in 8.2.1.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used independently of the other.Combiningvalues from the two systems may result in non-conf
5、ormancewith the standard.1.2.1 Within the text the inch-pound units are shown inbrackets.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health and environment
6、al practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Gui
7、des and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:D695 Test Method for Compressive Properties of RigidPlasticsD792 Test Methods for Density and Specific Gravity(Rela-tive Density)of Plastics by Displaceme
8、ntD883 Terminology Relating to PlasticsD3410/D3410M Test Method for Compressive Properties ofPolymer Matrix Composite Materials with UnsupportedGage Section by Shear LoadingD3171 Test Methods for Constituent Content of CompositeMaterialsD3878 Terminology for Composite MaterialsD5229/D5229M Test Meth
9、od for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer MatrixComposite MaterialsD5467/D5467M Test Method for Compressive Properties ofUnidirectional Polymer Matrix Composite Materials Us-ing a Sandwich BeamD6484/D6484M Test Method for Open-Hole CompressiveStrength of Polymer M
10、atrix Composite LaminatesD6507 Practice for Fiber Reinforcement Orientation Codesfor Composite MaterialsD6641/D6641M Test Method for Compressive Properties ofPolymer Matrix Composite Materials Using a CombinedLoading Compression(CLC)Test FixtureD7249/D7249M Test Method for Facing Properties of Sand-
11、wich Constructions by Long Beam FlexureE6 Terminology Relating to Methods of Mechanical TestingE132 Test Method for Poissons Ratio at Room TemperatureE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE456 Terminology Relating to Quality and Statistics3.Terminology3.1 Definitio
12、nsTerminology D3878 defines terms relatingto high-modulus fibers and their composites,as well as termsrelating to structural sandwich constructions.TerminologyD883 defines terms relating to plastics.Terminology E6 definesterms relating to mechanical testing.Terminology E456 andPractice E177 define t
13、erms relating to statistics.In the event ofa conflict between terms,Terminology D3878 shall haveprecedence over the other standards.3.2 Definitions of Terms Specific to This StandardNOTE1If the term represents a physical quantity,its analyticaldimensions are stated immediately following the term(or
14、letter symbol)infundamental dimension form,using the following ASTM Internationalstandard symbology for fundamental dimensions,shown within squarebrackets:M for mass,L for length,T for time,for thermodynamictemperature,and nd for non-dimensional quantities.Use of these1This test method is under the
15、jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.05 onStructural Test Methods.Current edition approved Aug.1,2017.Published September 2017.DOI:10.1520/D8066_D8066M-17.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Cons
16、hohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 symbols is restricted to analytical dimensions when used with squarebrackets,as the symbols may have other definitions when used without thebrackets