1、Designation:D 866 99(Reapproved 2004)An American National StandardStandard Specification forCrosslinked Styrene-Butadiene(SBR)Synthetic RubberJacket for Wire and Cable1This standard is issued under the fixed designation D 866;the number immediately following the designation indicates the year oforig
2、inal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon(e)indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification covers a crosslinked styrene-butadiene(SBR)synthet
3、ic rubber compound suitable for use asthe outer covering or jacket on insulated electrical wires orcables for heavy-duty service.1.2 This jacket is not recommended for installation at atemperature lower than 35C.1.3 Whenever two sets of values are presented,in differentunits,the values in the first
4、set are the standard,while those inparentheses are for information only.2.Referenced Documents2.1 ASTM Standards:2D 470 Test Methods for Crosslinked Insulations and Jacketsfor Wire and CableD 1711 Terminology Relating to Electrical Insulation3.Terminology3.1 DefinitionsFor definitions of terms used
5、in this speci-fication,refer to Terminology D 1711.3.2 Definitions of Terms Specific to This Standard:3.2.1 aging(act of),nexposure of materials to air at 70Cfor 168 h or oxygen at 70C for 96 h.4.Physical Properties4.1 The jacket shall conform to the requirements for physi-cal properties prescribed
6、in Table 1.5.Sampling5.1 Sample the jacket in accordance with Test MethodsD 470.6.Test Methods6.1 Test the jacket in accordance with Test Methods D 470.7.Keywords7.1 crosslinked jacket;rubber jacket;styrene-butadienejacket;synthetic rubber jacketASTM International takes no position respecting the va
7、lidity of any patent rights asserted in connection with any item mentionedin this standard.Users of this standard are expressly advised that determination of the validity of any such patent rights,and the riskof infringement of such rights,are entirely their own responsibility.This standard is subje
8、ct to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised,either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarter
9、s.Your comments will receive careful consideration at a meeting of theresponsible technical committee,which you may attend.If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards,at the address shown below.This standard is co
10、pyrighted by ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959,United States.Individual reprints(single or multiple copies)of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585(phone),610-832-9555(fax),or serviceastm.org(e-mail)
11、;or through the ASTM website(www.astm.org).1This specification is under the jurisdiction of ASTM Committee D09 onElectrical and Electronic Insulating Materials and is the direct responsibility ofSubcommittee D09.18 on Solid Insulations,Nonmetallic Shieldings,and Coveringsfor Electrical and Telecommu
12、nications Wires and Cables.Current edition approved March 1,2004.Published March 2004.Originallyapproved in 1946.Last previous edition approved in 1999 as D 866 99.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of
13、 ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.TABLE 1 Physical PropertiesAUnaged Requirements:Tensile strength,min,psi(MPa)1800(12.4)Elongation at rupture,min,%300Tension set,Bmax,%20Aged Requirements:After oxygen pressure test at 70 6 1C for 96 h:
14、Tensile strength,min,psi(MPa)1400(9.7)Elongation at rupture,min,%200After Air Oven Test at 70 6 1C for 168 h:Tensile strength,min,psi(MPa)1400(9.7)Elongation at rupture,min,%200AThe values specified are applicable only to jacket having a nominal wallthickness of 0.030 in.(0.76 mm)or greater.BSet in 2 in.(50 mm).1Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959,United States.