1、Designation:D581720Standard Practice forCarbon Black,PelletedReduction,Blending,and Drying ofGross Samples for Testing1This standard is issued under the fixed designation D5817;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year
2、 of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This practice describes the procedure for blending ofpelleted carbon black,the procedure for the reduction of grosssamp
3、les of pelleted carbon black to the appropriate size fortesting and the preparation of the sample for testing.Thesetechniques are intended to minimize variations in measuredcharacteristics between test samples.Standard terminologyrelating to carbon black samples is found in TerminologyD3053.The clas
4、sification system for carbon blacks used inrubber products can be found in Classification System D1765.1.2 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns,i
5、f any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internation
6、ally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D412 Test Metho
7、ds for Vulcanized Rubber and Thermoplas-tic ElastomersTensionD1506 Test Methods for Carbon BlackAsh ContentD1508 Test Method for Carbon Black,Pelleted Fines andAttritionD1509 Test Methods for Carbon BlackHeating LossD1510 Test Method for Carbon BlackIodine AdsorptionNumberD1511 Test Method for Carbo
8、n BlackPellet Size Distri-butionD1512 Test Methods for Carbon BlackpH ValueD1513 Test Method for Carbon Black,PelletedPour Den-sityD1514 Test Method for Carbon BlackSieve ResidueD1618 Test Method for Carbon Black ExtractablesTransmittance of Toluene ExtractD1619 Test Methods for Carbon BlackSulfur C
9、ontentD1765 Classification System for Carbon Blacks Used inRubber ProductsD1799 Practice for Carbon BlackSampling PackagedShipmentsD1900 Practice for Carbon BlackSampling Bulk Ship-mentsD2414 Test Method for Carbon BlackOil AbsorptionNumber(OAN)D3053 Terminology Relating to Carbon BlackD3191 Test Me
10、thods for Carbon Black in SBR(Styrene-Butadiene Rubber)Recipe and Evaluation ProceduresD3192 Test Methods for Carbon Black Evaluation in NR(Natural Rubber)D3265 Test Method for Carbon BlackTint StrengthD3493 Test Method for Carbon BlackOil AbsorptionNumber of Compressed Sample(COAN)D5230 Test Method
11、 for Carbon BlackAutomated Indi-vidual Pellet HardnessD6556 Test Method for Carbon BlackTotal and ExternalSurface Area by Nitrogen AdsorptionD7854 Test Method for Carbon Black-Void Volume at MeanPressure3.Summary of Test Methods3.1 Test Method AReduction of Sample Size:3.1.1 The gross bulk sample is
12、 poured through the rifflesample splitter.Aportion of the sample is reintroduced into thesplitter as many times as necessary to reduce the gross sampleto the size desired for the intended test portion.The test portionmay not be homogeneous.1This practice is under the jurisdiction of ASTM Committee D
13、24 on CarbonBlack and is the direct responsibility of Subcommittee D24.61 on Carbon BlackSampling and Statistical Analysis.Current edition approved June 1,2020.Published July 2020.Originally approvedin 1995.Last previous edition approved in 2019 as D5817 19.DOI:10.1520/D5817-20.2For referenced ASTM
14、standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 194
15、28-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technic
16、al Barriers to Trade(TBT)Committee.3.2 Test Method BBlending of Carbon Black:3.2.1 The gross sample is poured through the riffle samplesplitter a minimum of four times in a specific sequence toprepare a homogeneous test portion.The black must becross-blended to accomplish a homogeneous portion for test-ing.3.3 Test Method CDrying of Carbon Black:3.3.1 The sample must be dried before testing begins forthese test methods:Vulcanized Rubber and ThermoplasticElastomersTension(Test Methods D412),Ash(T