1、Designation:D620001(Reapproved 2017)Standard Test Method forDetermination of Cooling Characteristics of Quench Oils byCooling Curve Analysis1This standard is issued under the fixed designation D6200;the number immediately following the designation indicates the year oforiginal adoption or,in the cas
2、e of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method describes the equipment and theprocedure for evaluation of a quenching oils quen
3、chingcharacteristics by cooling rate determination.1.2 This test is designed to evaluate quenching oils in anon-agitated system.There is no correlation between these testresults and the results obtained in agitated systems.1.3 The values in SI units are to be regarded as the standard.1.3.1 Exception
4、The values in parentheses are provided forinformation only.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine th
5、e applicability of regulatory limitations prior to use.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issue
6、d by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D1744 Test Method for Determination of Water in LiquidPetroleum Products by Karl Fischer Reagent(Withdrawn2016)3E220 Test Method for Calibration of Thermocouples ByComparison Techniqu
7、esE230 Specification and Temperature-Electromotive Force(EMF)Tables for Standardized Thermocouples2.2 SAE Standards:4AMS 5665 Nickel Alloy Corrosion and Heat Resistant Bars,Forgings and Rings2.3 Japanese Industrial Standards(JIS):5JIS K 2242-1980 Heat Treating OilJIS K 6753-1977 Di-2-ethylhexyl Phth
8、alate3.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 cooling curve,nthe cooling curve is a graphicalrepresentation of the cooling time(t)-temperature(T)re-sponse of the probe(see 7.3).An example is illustrated in PartB of Fig.1.3.1.2 cooling curve analysis,nthe process of quant
9、ifyingthe cooling characteristics of a heat treating oil based on thetemperature versus time profile obtained by cooling a pre-heated metal probe assembly(see Fig.2)under standardconditions.3.1.3 cooling rate curve,nThe cooling rate curve isobtained by calculating the first derivative(dT/dt)of theco
10、oling time-temperature curve.An example is illustrated inPart B of Fig.1.3.1.4 heat treating oil,na hydrocarbon containingproduct,often derived from petroleum base stock,that is usedto mediate heat transfer between heated metal,such as austen-itized steel,to control the microstructure that is formed
11、 uponcooling and also control distortion and minimize crackingwhich may accompany the cooling process.3.1.5 quench severity,nthe ability of a quenching mediumto extract heat from a hot metal.64.Summary of Test Method4.1 Determine the nickel alloy probe assemblys coolingtime versus temperature after
12、placing the assembly in a furnace1This test method is under the jurisdiction of ASTM Committee D02 onPetroleum Products,Liquid Fuels,and Lubricants and is the direct responsibility ofSubcommittee D02.L0.06 on Non-Lubricating Process Fluids.Current edition approved Oct.1,2017.Published November 2017.
13、Originallyapproved in 1997.Last previous edition approved in 2012 as D620001(2012).DOI:10.1520/D6200-01R17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards
14、Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.4Available from Society of Automotive Engineers(SAE),400 CommonwealthDr.,Warrendale,PA 15096-0001,http:/www.sae.org.5Available from Japanese Standards Organization(JSA),4-1-24
15、 AkasakaMinato-Ku,Tokyo,107-8440,Japan,http:/www.jsa.or.ja.6Boyer,H.E.and Cary,P.R.,Quenching and Distortion Control,ASMInternational,Materials Park,OH,1988,p.162.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard w
16、as developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 and heating to 850 C(1562 F)and then quenching in a heattreating oil.The temperature inside the probe assembly and thecooling times are recorded at selected time intervals to estab-lish a cooling temperature versu