1、Designation:D593017Standard Test Method forThermal Conductivity of Plastics by Means of a TransientLine-Source Technique1This standard is issued under the fixed designation D5930;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the ye
2、ar of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the determination of the thermalconductivity of plastics over a temperature range from 40 to4
3、00C.It is possible to measure the thermal conductivity offilled and unfilled thermoplastics,thermosets,and rubbers inthe range from 0.08 to 2.0 W/m.K.1.2 The values stated in SI units shall be regarded asstandard.1.3 This standard does not purport to address the safetyconcerns,if any,associated with
4、 its use.It is the responsibilityof the user of this standard to establish proper safety andhealth practices and determine the applicability of regulatorylimitations prior to use.NOTE1There is no known ISO equivalent to this test method.1.4 This international standard was developed in accor-dance wi
5、th internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2C
6、177 Test Method for Steady-State Heat Flux Measure-ments and Thermal Transmission Properties by Means ofthe Guarded-Hot-Plate ApparatusC518 Test Method for Steady-State Thermal TransmissionProperties by Means of the Heat Flow Meter ApparatusC1113 Test Method for Thermal Conductivity of Refracto-ries
7、 by Hot Wire(Platinum Resistance ThermometerTechnique)D618 Practice for Conditioning Plastics for TestingD883 Terminology Relating to PlasticsD2717 Test Method for Thermal Conductivity of LiquidsE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE1225 Test Method for Thermal Co
8、nductivity of SolidsUsing the Guarded-Comparative-Longitudinal Heat FlowTechnique3.Terminology3.1 DefinitionsTerminology used in this standard is inaccordance with Terminology D883.3.2 Definitions of Terms Specific to This Standard:3.2.1 temperature transient,nthe temperature rise associ-ated with t
9、he perturbation of a system,initially at a uniformtemperature.The system does not attain thermal equilibriumduring the transient.3.2.2 thermal conductivity,nthe time rate of steady heatflow/unit area through unit thickness of a homogeneous mate-rial in a direction perpendicular to the surface induce
10、d by a unittemperature difference.3.2.2.1 DiscussionWhere other modes of heat transfer arepresent in addition to conduction,such as convection andradiation,this property often is referred to as the apparentthermal conductivity,app.3.2.2.2 DiscussionThermal conductivity must be associ-ated with the c
11、onditions under which it is measured,such astemperature and pressure,as well as the compositional varia-tion of the material.It is possible that thermal conductivity willvary with direction and orientation of the specimen since somematerials are not isotropic with respect to thermal conductivity.In
12、the case of thermoset polymers,it is possible that thermalconductivity will vary with the extent of cure.3.2.3 thermal diffusivitya heat-transport property given bythe thermal conductivity divided by the thermal mass,which isa product of the density and the heat capacity.3.3 Symbols:3.3.1 CProbe con
13、stant.3.3.2 Thermal conductivity,W/m.K.3.3.3 QHeat output per unit length,W/m.3.3.4 T2The temperature(K)recorded at time t2.1This test method is under the jurisdiction of ASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.30 on Thermal Properties.Current edition appro
14、ved Aug.1,2017.Published August 2017.Originallyapproved in 1997.Last previous edition approved in 2016 as D5930-16.DOI:10.1520/D5930-17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume inform
15、ation,refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance w
16、ith internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 3.3.5 T1The temperature(K)recorded at time t1.3.4 Subscript:3.4.1 avaverage.3.4.2 appapparent.3.4.3 refreference.4.Summary of Test Method4.1 Line-Source TechniqueThis is a transient method fordetermining thermal conductivity(1,2).3A line sou