1、Designation:D581304(Reapproved 2012)An American National StandardStandard Specification forCured-In-Place Thermosetting Resin Sewer Piping Systems1This standard is issued under the fixed designation D5813;the number immediately following the designation indicates the year oforiginal adoption or,in t
2、he case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification covers cured-in-place thermosettingresin pipe(CIPP),4 through 132-in.(10
3、0 through 3353-mm)equivalent diameter,for use in gravity flow systems forconveying sanitary sewage,storm water,and certain industrialwastes.This specification is suited for the evaluation andtesting of materials used in the rehabilitation of existing pipesby the installation and cure of a resin-impr
4、egnated fabric liner.1.2 This specification can also be extended to covermanholes,pump stations,wetwells,vaults,storage tanks,andother similar structures where a cured in place liner usingthermosetting resin is applicable.1.3 The values stated in inch-pound units are to be regardedas standard.The va
5、lues given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.NOTE1There are no ISO standards covering the primary subjectmatter of this specification.1.4 The following safety hazards caveat pertains only to thetest methods po
6、rtion,Section 8,of this specification:Thisstandard does not purport to address all of the safety concerns,if any,associated with its use.It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions
7、 prior to use.2.Referenced Documents2.1 ASTM Standards:2D543 Practices for Evaluating the Resistance of Plastics toChemical ReagentsD638 Test Method for Tensile Properties of PlasticsD695 Test Method for Compressive Properties of RigidPlasticsD790 Test Methods for Flexural Properties of Unreinforced
8、and Reinforced Plastics and Electrical Insulating Materi-alsD883 Terminology Relating to PlasticsD1600 Terminology forAbbreviated Terms Relating to Plas-ticsD1682 Methods of Test for Breaking Load and Elongation ofTextile Fabrics3D3039/D3039M Test Method for Tensile Properties of Poly-mer Matrix Com
9、posite MaterialsD3567 Practice for Determining Dimensions of“Fiberglass”(Glass-Fiber-Reinforced Thermosetting Resin)Pipe andFittingsD3681 Test Method for Chemical Resistance of“Fiberglass”(GlassFiberReinforced Thermosetting-Resin)Pipe in aDeflected ConditionD4814 Specification for Automotive Spark-I
10、gnition EngineFuelF412 Terminology Relating to Plastic Piping SystemsF1216 Practice for Rehabilitation of Existing Pipelines andConduits by the Inversion and Curing of a Resin-Impregnated TubeF1743 Practice for Rehabilitation of Existing Pipelines andConduits by Pulled-in-Place Installation of Cured
11、-in-PlaceThermosetting Resin Pipe(CIPP)F2019 Practice for Rehabilitation of Existing Pipelines andConduits by the Pulled in Place Installation of GlassReinforced Plastic(GRP)Cured-in-Place ThermosettingResin Pipe(CIPP)3.Terminology3.1 GeneralDefinitions are in accordance with Termi-nologies D883 and
12、 F412.Abbreviations are in accordance withTerminology D1600,unless otherwise indicated.3.2 Definitions of Terms Specific to This Standard:3.2.1 cured-in-place pipe(CIPP)hollow cylinder or shapeconsisting of a fabric with cured(cross-linked)thermoset resin;interior or exterior plastic tube coatings,o
13、r both,may beincluded;this pipe is formed within and takes the shape of anexisting conduit or structure.1This specification is under the jurisdiction of ASTM Committee D20 onPlastics and is under the direct responsibility of Subcommittee D20.23 onReinforced Plastic Piping Systems and Chemical Equipm
14、ent.Current edition approved Oct.1,2012.Published October 2012.Originallyapproved in 1995.Last previous edition approved in 2008 as D581304(2008).DOI:10.1520/D5813-04R12.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual B
15、ook of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Withdrawn.The last approved version of this historical standard is referencedon www.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United
16、States1 3.2.2 delaminationseparation of coating or layers of theCIPP,or both.3.2.3 dry spota fabric area of the finished CIPP which isdeficient or devoid of resin.3.2.4 fabric tubea flexible material formed into a tubularshape which during the installation process is saturated withresin and holds the resin in place during the cure.3.2.5 fully deteriorated pipethe original pipe is not struc-turally sound and cannot support soil and live loads or isexpected to reach this condition over the design