1、Designation:D634114aStandard Test Method forDetermination of the Linear Coefficient of ThermalExpansion of Plastic Lumber and Plastic Lumber ShapesBetween 30 and 140F(34.4 and 60C)1This standard is issued under the fixed designation D6341;the number immediately following the designation indicates th
2、e year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This test method covers the determination of the coef-fi
3、cient of linear thermal expansion for plastic lumber andplastic lumber shapes to two significant figures.The determi-nation is made by taking measurements with a caliper at threediscrete temperatures.At the test temperatures and under thestresses imposed,the plastic lumber shall have a negligiblecre
4、ep or elastic strain rate,or both,insofar as these propertieswould significantly affect the accuracy of the measurements.1.1.1 This test method details the determination of the linearcoefficient of thermal expansion of plastic lumber and plasticlumber shapes in their“as manufactured”form.As such,thi
5、s isa test method for evaluating the properties of plastic lumber orshapes as a product and not a material property test method.1.2 The thermal expansion of plastic lumber and shapes iscomposed of a reversible component on which it is possible tosuperimpose changes in length due to changes in moistu
6、recontent,curing,loss of plasticizer or solvents,release ofstresses,phase changes,voids,inclusions,and other factors.This test method is intended to determine the coefficient oflinear thermal expansion under the exclusion of non-linearfactors as far as possible.In general,it will not be possible toe
7、xclude the effect of these factors completely.For this reason,the test method can be expected to give a reasonable approxi-mation but not necessarily precise determination of the linearcoefficient of thermal expansion.1.3 Plastic lumber and plastic lumber shapes are currentlymade predominately with
8、recycled plastics where the productis non-homogeneous in the cross-section.However,it ispossible that this test method will also be applicable to similarmanufactured plastic products made from virgin resins or otherplastic composite materials.1.4 The values stated in inch-pound units are to be regar
9、dedas the standard.The SI units given in parentheses are forinformation only.1.5 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine
10、 the applica-bility of regulatory limitations prior to use.NOTE1There is no known ISO equivalent to this standard.2.Referenced Documents2.1 ASTM Standards:2D883 Terminology Relating to PlasticsD4065 Practice for Plastics:Dynamic Mechanical Proper-ties:Determination and Report of ProceduresD5033 Guid
11、e for Development ofASTM Standards Relatingto Recycling and Use of Recycled Plastics(Withdrawn2007)3E831 Test Method for Linear Thermal Expansion of SolidMaterials by Thermomechanical Analysis3.Terminology3.1 Definitions:3.1.1 plastic lumber,na manufactured product made pri-marily from plastic mater
12、ials(filled or unfilled),typically usedas a building material for purposes similar to those of tradi-tional lumber,which is usually rectangular in cross-section.(Terminology D883)3.1.1.1 DiscussionPlastic lumber is typically supplied insizes similar to those of traditional lumber board,timber anddim
13、ension lumber;however the tolerances for plastic lumberand for traditional lumber are not necessarily the same.(Terminology D883)3.1.2 plastic lumber shape,na plastic lumber productwhich is generally not rectangular in cross-section.3.1.3 resin,na solid or pseudosolid organic material oftenof high m
14、olecular weight,which exhibits a tendency to flow1This test method is under the jurisdiction of ASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.20 on Plastic Lumber.Current edition approved Aug.1,2014.Published September 2014.Originallyapproved in 1998.Last previou
15、s edition approved in 2014 as D6341-14.DOI:10.1520/D6341-14A.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The
16、last approved version of this historical standard is referenced onwww.astm.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 when subjected to stress,usually has a softening or meltingrange,and usually fractures conchoidally.(Terminology D883)3.1.3.1 DiscussionIn a broad sense,the term is used todesignate any polymer that is a basic material for plastics.(1982)3.2 Addi