1、Designation:D580500(Reapproved 2019)Standard Test Methods forRubberDetermination of Carbon Black in Masterbatches1This standard is issued under the fixed designation D5805;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of l
2、ast revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 These test methods cover the determination of theamount of carbon black in a masterbatch and cover emulsionSBR-carbon black
3、mixtures,but may be applicable to otherpolymers.Three test methods are included:SectionsInert Atmosphere Pyrolysis3 10Vacuum Pyrolysis11 17Thermogravimetric Analyzer18 24NOTE1The nomenclature used in these test methods is in accordancewith Practice D1418.1.2 The values stated in SI units are to be r
4、egarded as thestandard.The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practic
5、es and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Re
6、com-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D1418 PracticeforRubberandRubberLaticesNomenclatureD6370 Test Method for RubberCompositional Analysisby Thermogravimetry(TGA)TEST METHOD ACARBON BLACKInert Atmosph
7、ere Pyrolysis Test Method3.Summary of Test Method3.1 The prepared dried sample and a sample of standardSBR black determinate are tested in triplicate.The samples areweighed accurately into tared crucibles and then placed in acombustion tube at 550C,which is continuously flushed withCO2until the rubb
8、er hydrocarbon is distilled.The crucibles andcontents are cooled in a desiccator,weighed,then inserted intoa muffle furnace at 550C until all carbonaceous material isburned.The crucible and contents are again cooled in adesiccator and weighed.The percentage of carbon black iscalculated from the weig
9、hts.4.Significance and Use4.1 The carbon black content of an unvulcanized black oroil-black SBR masterbatch may be determined by this testmethod if an inert(CO2)atmosphere and a determinate(seeNote 2)of known carbon black content are available.NOTE2Determinate black masterbatch may be prepared by ca
10、refuladdition of exact amounts of rubber and carbon black on a mill.Analternative would be a thorough blending of a quantity of black master-batch and determination of the carbon black by use of a previouslyestablished determinate.5.Apparatus5.1 Drying Oven.5.2 Porcelain Crucibles,No.00000,tared.5.3
11、 Weighing Bottles,tared.5.4 Fused Alumina Combustion Boats.35.5 Combustion Tubes.45.6 Combustion Furnace.1These test methods are under the jurisdiction of ASTM Committee D11 onRubber and Rubber-like Materials and are the direct responsibility of SubcommitteeD11.11 on Chemical Analysis.Current editio
12、n approved Jan.1,2019.Published February 2019.Originallyapproved in 1995.Last previous edition approved in 2014 as D5805 00(2014).DOI:10.1520/D5805-00R19.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStand
13、ards volume information,refer to the standards Document Summary page onthe ASTM website.3Alundum No.3 combustion boats have been found satisfactory for this purpose.4The sole source of supply of the combustion tube known to the committee atthis time is the McDaniel high-temperature combustion tube,3
14、0 in.(762 mm)longby 1 in.(25.4 mm)in diameter available from Dunlap and Co.,623 Staring Lane,Baton Rouge,LA 70810.This tube will accommodate a maximum of twocombustion boats containing six samples each within the heated area of the furnace.If you are aware of alternative suppliers,please provide thi
15、s information to ASTMInternational Headquarters.Your comments will receive careful consideration at ameeting of the responsible technical committee,1which you may attend.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international sta
16、ndard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 6.Reagents6.1 Purity of ReagentsReagent grade chemicals shall beused in all tests.Unless otherwise indicated,it is intended thatall reagents conform to the specifications of the Committee onAnalytical Reage