资源描述

1、Designation:D559122Standard Test Method forThermal Shrinkage Force of Yarn and Cord With a ThermalShrinkage Force Tester1This standard is issued under the fixed designation D5591;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the ye

2、ar of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers preparation and procedures tomeasure the thermal shrinkage force of yarns and cords in air.1.

3、2 This test method is applicable to measurement of thethermal shrinkage force of yarns and cords whose shrinkageforce at 180 6 2 C(355 6 4 F)in air does not exceed 20 N(4 lbf).This test method is applicable to nylon,polyester,andaramid yarns and cords within the applicable range of thermalshrinkage

4、force,as well as to comparable yarns and cords fromother polymers.1.2.1 Test specimens may be taken from yarn or cordpackages,or retrieved from fabrics.1.3 The values stated in SI units are to be regarded asstandard.The values given in parentheses after SI units areprovided for information only and

5、are not considered standard.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory l

6、imitations prior to use.Specific hazards statements are given in Section 8.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Re

7、com-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D123 Terminology Relating to TextilesD885/D885M Test Methods for Tire Cords,Tire CordFabrics,and Industrial Filament Yarns Made from Manu-factured Organic-Base Fib

8、ersD2258/D2258M Practice for Sampling Yarn for TestingD6477 Terminology Relating to Tire Cord,Bead Wire,HoseReinforcing Wire,and Fabrics(Withdrawn 2022)33.Terminology3.1 Definitions:3.1.1 For definitions of terms relating to tire cord,bead wire,hose wire,and tire cord fabrics,refer to Terminology D6

9、477.3.1.1.1 The following terms are relevant to this standard:adhesive-treated tire cord;cord;greige cord;greige tire cord;pneumatic tire;retraction,in yarns and cords;standard atmo-sphere for testing textiles;thermal shrinkage force;thermalshrinkage force tester;tire.3.2 For definitions of other te

10、rms related to textiles,refer toTerminology D123.3.2.1 The following terms are relevant to this standard:thermal shrinkage force;thermal shrinkage force tester;yarn.4.Summary of Test Method4.1 A specified length of yarn or cord is conditioned in arelaxed state,mounted with a pretension of 5 mN/tex 6

11、 1mN tex(0.05 gf/den 6 0.01 gf/den),then exposed to dry heatat a temperature of 180 C 6 2 C(355 F 6 4 F)for120 s 6 5 s.4.2 The shrinkage force induced in the specimen is readfrom the tester.5.Significance and Use5.1 This test method may be used for the acceptance testingof commercial shipments of ya

12、rns and cords.5.1.1 If there are differences of practical significance be-tween reported test results for two laboratories(or more),comparative tests should be performed to determine if there isa statistical bias between them,using competent statisticalassistance.As a minimum,test samples should be

13、used that are1This test method is under the jurisdiction ofASTM Committee D13 on Textilesand is the direct responsibility of Subcommittee D13.19 on Industrial Fibers andMetallic Reinforcements.Current edition approved June 1,2022.Published July 2022.Originally approvedin 1995.Last previous edition a

14、pproved in 2016 as D5591 04(2016).DOI:10.1520/D5591-22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last a

15、pproved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization e

16、stablished in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1as homogeneous as possible,that are drawn from the materialfrom which the disparate test results were obtained,and thatare randomly assigned in equal numbers to each laboratory fortesting.Other materials with established test values may beused for this purpose.The test results from the two laboratoriess