1、Designation:D5687/D5687M95(Reapproved 2015)Standard Guide forPreparation of Flat Composite Panels with ProcessingGuidelines for Specimen Preparation1This standard is issued under the fixed designation D5687/D5687M;the number immediately following the designation indicates theyear of original adoptio
2、n or,in the case of revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This guide provides guidelines to facilitate the properpreparation of laminates an
3、d test specimens from fiber-reinforced organic matrix composite prepregs.The scope islimited to organic matrices and fiber reinforcement in unidi-rectional(tape)or orthagonal weave patterns.Other forms mayrequire deviations from these general guidelines.Other pro-cessing techniques for test coupon p
4、reparation,for example,pultrusion,filament winding and resin-transfer molding,arenot addressed.1.2 Specimen preparation is modeled as an 8-step processthat is presented in Fig.1 and Section 8.Laminate consolida-tion techniques are assumed to be by press or autoclave.Thispractice assumes that the mat
5、erials are properly handled by thetest facility to meet the requirements specified by the materialsupplier(s)or specification,or both.Identification and infor-mation gathering guidelines are modeled after Guide E1309.Test specimens shall be directly traceable to material used asdesignated in Guide E
6、1434.Proper test specimen identificationalso includes designation of process equipment,process steps,and any irregularities identified during processing.1.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.Within the text theinch-pound units are shown
7、 in brackets.The values stated ineach system are not exact equivalents;therefore,each systemmust be used independently of the other.Combining valuesfrom the two systems may result in nonconformance with thestandard.1.4 This standard does not purport to address all of thesafety concerns,if any,associ
8、ated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2C297/C297M Test Method for Flatwise Tensile Strength ofSandwi
9、ch ConstructionsD123 Terminology Relating to TextilesD792 Test Methods for Density and Specific Gravity(Rela-tive Density)of Plastics by DisplacementD883 Terminology Relating to PlasticsD2734 Test Methods for Void Content of Reinforced PlasticsD3163 Test Method for Determining Strength of Adhesively
10、Bonded Rigid Plastic Lap-Shear Joints in Shear by Ten-sion LoadingD3171 Test Methods for Constituent Content of CompositeMaterialsD3531 Test Method for Resin Flow of Carbon Fiber-EpoxyPrepregD3878 Terminology for Composite MaterialsD3990 Terminology Relating to Fabric DefectsD4850 Terminology Relati
11、ng to Fabrics and Fabric TestMethodsD5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer MatrixComposite MaterialsE1237 Guide for Installing Bonded Resistance Strain GagesE1309 GuideforIdentificationofFiber-ReinforcedPolymer-Matrix Composite Materials i
12、n Databases(With-drawn 2015)3E1434 Guide for Recording Mechanical Test Data of Fiber-Reinforced Composite Materials in Databases(Withdrawn2015)33.Terminology3.1 DefinitionsTerminology D3878 defines terms relatingto high-modulus fibers and their composites.TerminologyD883 defines terms relating to pl
13、astics.Terminology D123defines textile related terms.Terminology D4850 defines terms1This guide is under the jurisdiction of ASTM Committee D30 on CompositeMaterials and is the direct responsibility of Subcommittee D30.04 on Lamina andLaminate Test Methods.Current edition approved Nov.1,2015.Publish
14、ed December 2015.Originallyapproved in 1995.Last previous edition approved in 2007 as D5687/D5687M-95(2007).DOI:10.1520/D5687_D5687M-95R15.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume inf
15、ormation,refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 relating to fabric.In the event o
16、f a conflict between terms,Terminology D3878 shall have precedence over the otherstandards.3.2 Description of Trems Used in This StandardThe termsused in this guide may conflict with general usage.There is notyet an established consensus concerning the use of these terms.The following descriptions are intended only for use in thisguide.3.2.1 bag,vthe process of enclosing the ply layers withina flexible container.See lay-up.3.2.2 base plate,na flat plate on which a laminate is laidup usually made