1、Designation:D480414Standard Test Method forDetermining the Flammability Characteristics of NonrigidSolid Plastics1This standard is issued under the fixed designation D4804;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of l
2、ast revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This fire-test-response test methods describe small-scalelaboratory procedures for determining the comparative burningchara
3、cteristics of solid plastic materials that,due to specimenthinness and nonrigidity,distort,shrink,and/or are consumedup to holding clamp when tested using Test Method D3801.Aflame is applied to the base of specimens held in a verticalposition and the extinguishing times are determined uponremoval of
4、 the test flame.1.2 The classification system described in Appendix X1 isintended for quality assurance and the preselection of compo-nent materials for products.1.3 This standard measures and describes the response ofmaterials,products,or assemblies to heat and flame undercontrolled conditions,but
5、does not by itself incorporate allfactors required for fire hazard or fire risk assessment of thematerials,products,or assemblies under actual fire conditions.NOTE1This standard is equivalent to ISO 9773,IEC 60695-11-10,and UL 94(Section 11).NOTE2For rate of burning of nonrigid solid plastics in a h
6、orizontalposition,formerly Test Method B of this test method,see Test MethodD635.1.4 This test method is not intended to cover plastics whenused as materials for building construction or finishing.1.5 Fire testing is inherently hazardous.Adequate safe-guards for personnel and property shall be emplo
7、yed inconducting these tests.1.6 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations pr
8、ior to use.For specific hazardstatements,see 6.1.1.2.Referenced Documents2.1 ASTM Standards:2D635 Test Method for Rate of Burning and/or Extent andTime of Burning of Plastics in a Horizontal PositionD883 Terminology Relating to PlasticsD3801 Test Method for Measuring the Comparative BurningCharacter
9、istics of Solid Plastics in a Vertical PositionD5025 Specification for Laboratory Burner Used for Small-Scale Burning Tests on Plastic MaterialsD5207 Practice for Confirmation of 20mm(50W)and125mm(500W)Test Flames for Small-Scale BurningTests on Plastic MaterialsE176 Terminology of Fire StandardsE69
10、1 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method2.2 ISO Standards:ISO 977398 PlasticsDetermination of Burning Behav-iour of Thin Flexible Vertical Specimens in Contact Witha Small Flame Ignition Source33.Terminology3.1 DefinitionsFor terms relating to pla
11、stics,the defini-tions in this test method are in accordance with TerminologyD883.For definitions of fire-related terms used in this testmethod,refer to Terminology E176.3.2 Definitions of Terms Specific to This Standard:3.2.1 flame-application timethe time in seconds that theflame from the burner i
12、s in contact with the specimen.3.2.2 flaming materialflaming drips or particles from thespecimen which ignite the dry,absorbent 100%surgical cottonplaced 300 mm 6 10 mm below the test specimen.3.2.3 afterflamepersistence of flaming of a material,afterthe ignition source has been removed.1This test m
13、ethod is under the jurisdiction of ASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.30 on Thermal Properties.Current edition approved Dec.1,2014.Published January 2015.Originallyapproved in 1988.Last previous edition approved in 2009 as D4804 09.DOI:10.1520/D4804-14
14、.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute(ANSI),25 W.
15、43rd St.,4th Floor,New York,NY 10036,http:/www.ansi.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 3.2.4 afterflame timethe length of time for which a mate-rial continu
16、es to flame,under specified conditions,after theignition source has been removed.3.2.5 afterglowpersistence of glowing of a material,aftercessation of flaming or,if no flaming occurs,after removal ofthe ignition source.3.2.6 afterglow timethe length of time for which a mate-rial continues to glow under specified test conditions,after theignition source has been removed or cessation of flaming,orboth.3.2.7 flameto undergo combustion in the gaseous phasewith emission of light.3.2.8 glowvisible lig