1、Designation:D413807a(Reapproved 2022)Standard Practices forMeasurement of Dry Film Thickness of Protective CoatingSystems by Destructive,Cross-Sectioning Means1This standard is issued under the fixed designation D4138;the number immediately following the designation indicates the year oforiginal ado
2、ption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This practice describes the measurement of dry filmthickness of coating films
3、by microscopic observation ofprecision angular cuts in the coating film.Use of theseprocedures may require repair of the coating film.This practiceis intended to supplement the manufacturers instructions forthe manual operation of the gages and is not intended to replacethem.It includes definitions
4、of key terms,referencedocuments,the significance and use of the practice,and theadvantages and limitations of the instruments.1.2 Three procedures are provided for measuring dry filmthickness of protective coating systems:1.2.1 Procedure AUsing groove cutting instruments.1.2.2 Procedure BUsing grind
5、ing instruments.1.2.3 Procedure CUsing drill bit instruments.1.3 These procedures are not applicable for soft or ductilesubstrates that may deform under the test gage cutting tip.Thesubstrate should be sufficiently rigid to prevent deformation ofthe coating during the cutting process.The surface may
6、 be flator moderately curved.Pipes as small as 25 mm(1 in.)indiameter may be measured in the axial direction.1.4 Individual coats in a multicoat system where there is adiscernible visual difference between coats or the overallthickness of a coating system can be measured by theseprocedures.1.5 The r
7、ange of thickness measurement is typically 2 to2000 microns(0.1 to 80 mils)and depends upon the cuttingangle of the blade.1.6 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.7 This standard does not purport to address all of t
8、hesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.8 This international standard was developed in accor-dan
9、ce with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standar
10、ds:2D823 Practices for Producing Films of Uniform Thicknessof Paint,Coatings and Related Products on Test PanelsD1005 Test Method for Measurement of Dry-Film Thick-ness of Organic Coatings Using MicrometersD7091 Practice for Nondestructive Measurement of DryFilm Thickness of Nonmagnetic Coatings App
11、lied toFerrous Metals and Nonmagnetic,Nonconductive Coat-ings Applied to Non-Ferrous Metals3.Terminology3.1 Definitions of Terms:3.1.1 accuracy,nthe measure of the magnitude of errorbetween the result of a measurement and the true thickness ofthe item being measured.3.1.2 dry film thickness,nthe thi
12、ckness of a coating(orcoating layers)as measured from the surface of the substrate.3.1.3 micrometre(micron),none one-thousandths of amillimetre(0.001 mm);25.4 microns=1 mil.3.1.4 mil,nan imperial unit of measure;one one-thousandths of an inch(0.001 in.);1 mil=25.4 microns.3.1.5 reticle,na scale on t
13、ransparent material fitted at thefocal plane of the eyepiece of the microscope for the purposeof measuring the width of a feature within the image.4.Summary of Practice4.1 The three procedures are based on measurement of dryfilm thickness by observation of the width of angular cuts in the1These prac
14、tices are under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings,Materials,and Applications and are the direct responsibilityof Subcommittee D01.23 on Physical Properties of Applied Paint Films.Current edition approved June 1,2022.Published June 2022.Originallyapproved in 1982.Las
15、t previous edition approved in 2017 as D4138 07a(2017).DOI:10.1520/D4138-07AR22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe
16、 ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1coating through a microscope having a built-in reticle with asc