1、Designation:D4333/D4333M05(Reapproved 2010)1Standard Test Method for theCompatibility of Mechanical Pump Dispenser Components1This standard is issued under the fixed designation D4333/D4333M;the number immediately following the designation indicates theyear of original adoption or,in the case of rev
2、ision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1NOTEUnits information was corrected editorially in March 2011.1.Scope1.1 This test method covers testing of the com
3、ponents ofmechanical pump dispensers(spray or flow types)for compat-ibility with products.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used independentl
4、y of the other.Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 This standard may involve hazardous materials,opera-tions,and equipment.This standard does not purport toaddress all of the safety concerns,if any,associated with itsuse.It is the responsibility of
5、 the user of this standard toconsult and establish appropriate safety and health practicesand determine the applicability of regulatory limitations priorto use.2.Significance and Use2.1 This test method identifies the compatibility of themechanical pump dispenser components with consumer-typeproduct
6、s.3.Apparatus3.1 Balance,accurate to 1 mg.3.2 Micrometers,or calipers or other appropriate instru-ments,capable of measuring dimensions of test specimens to0.025 mm 0.001 in.3.3 Glass Containers,with covers,suitable for immersingtest specimens in test products.3.4 Oven,with chamber capable of mainta
7、ining temperaturewithin 62C 63.6F of the specified test temperatures.4.Test Specimen4.1 At least three individual components should be used foreach part tested with each product involved at each testcondition.4.2 At least three individual components are used as con-trols at each test condition.4.3 I
8、ndividual unassembled components shall be clean andpreviously unused.5.Conditioning5.1 Condition test specimens at 23 6 3C 73.46 5.4F forat least 4 h prior to testing.If test specimen conditioning is notpossible,the environmental conditioning of the test specimenstested should be included in the rep
9、ort as discussed in 7.1.5.2 Test conditions shall be an elevated temperature of 45 63C 113 6 5.4F and an ambient room temperature of 23 63C 73.4 6 5.4F.If a different temperature is used,thisshould be noted in the test report discussed in 7.1.6.Procedure6.1 Dimensional and Weight Changes:6.1.1 Prior
10、 to immersion into the product,weigh the partand record as W1(see 7).Measure the thickness or overalllength of the part to the nearest 0.025 mm 0.001 in.of eachcomponent depending on which of these dimensions are mostimportant(for example,thickness for a gasket or liner,andoverall length for a molde
11、d component).Optionally,measure adiameter of the part to its nearest 0.025 mm 0.001 in.Reportthe data as initial dimension D1(see 7).This data is reportedas a mean value of the dimension for the components measuredfor that particular part.6.1.2 Maintain at least three test specimens as visual com-pa
12、rison controls.Do not immerse these control test specimensin any solution and store at each test condition.Label thestorage container of these test specimens as control.6.1.3 Place the test specimens in appropriate containers forthe solutions being used and allow the test specimens to betotally imme
13、rsed in fresh test product for 7 days in each testcondition.Several test specimens of a given material may be1This test method is under the jurisdiction of ASTM Committee D10 onPackaging and is the direct responsibility of Subcommittee D10.33 on MechanicalDispensers.Current edition approved Oct.1,20
14、10.Published March 2011.Originallyapproved in 1984.Last previous edition approved in 2005 as D4333 05.DOI:10.1520/D4333_D4333M-05R10E01.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 immersed in the same container provided sufficient pro
15、duct isavailable for the total surface area exposed.Cover the con-tainer.NOTE1When the components being tested are of the same type but ofdifferent material,it is recommended that separate glass containers areused for each material for the purpose of eliminating unplanned materialinteractions and fo
16、r ease of identification.6.1.4 After 7 days,remove all glass containers of testspecimens from the 45C environment,and allow the testspecimens to equilibrate to room temperature 23C for aminimum of 4 h.6.1.5 Carefully remove each test specimen from the glasscontainer,wipe dry,and remeasure the dimension(s)on eachpart as they were measured in 6.1.1.Be careful not to damageor distort the parts during removal.Measure parts immediately.Report the mean value of the dimensions measured at this timeas D