1、Designation:D331312Standard Test Method forCarbon BlackIndividual Pellet Hardness1This standard is issued under the fixed designation D3313;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parenth
2、eses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers a method for measuring thehardness of individual pellets of carbon black.1.2 The values stated in SI units are to be regarded as the
3、standard.The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica
4、-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2D1511 Test Method for Carbon BlackPellet Size Distri-butionD1799 Practice for Carbon BlackSampling PackagedShipmentsD1900 Practice for Carbon BlackSampling Bulk Ship-mentsD4483 Practice for Evaluating Precision
5、for Test MethodStandards in the Rubber and Carbon Black ManufacturingIndustriesD5230 Test Method for Carbon BlackAutomated Indi-vidual Pellet HardnessE11 Specification for Woven Wire Test Sieve Cloth and TestSieves3.Summary of Test Method3.1 A sample of carbon black is passed through two sievesto is
6、olate a fraction of uniform size.The most spherical pelletsfrom this portion are selected and brought into contact with ameasuring device as force is applied.Pellet hardness is themaximum force required to crush the pellets.4.Significance and Use4.1 Pellet hardness is related to several carbon black
7、 char-acteristics.Among these are mass strength and attrition.Thesubsequent level of dispersion obtained in some mixed com-pounds containing the carbon black may be affected by pellethardness.Acceptable pellet hardness must be agreed to by theuser and the producer.NOTE1Test Method D5230 is the prefe
8、rred standard for testing ofindividual pellet hardness.It is recognized that Test Method D3313 relieson operator judgement,thus adding an additional source of variation forthis test.5.Apparatus5.1 Pellet-Hardness Tester,3of a type capable of measuringthe pellet hardness of the individual pellet in g
9、rams-force(centinewtons).A suitable tester must exhibit the followingcharacteristics:5.1.1 Initial contact force must be applied so that the forcearea rests lightly on the pellet before proceeding,5.1.2 It must be capable of applying force at a constant rate,5.1.3 It must possess an accurate means o
10、f measuring theapplied force,and5.1.4 During the test,the applied force and base plate mustbe controlled so as not to cause the pellet to move or roll priorto crushing.NOTE2A two-pan torsion balance with 100-g dial and transparentfoot mounted so it can be moved directly over the pellet will serve to
11、convert a balance to a pellet hardness tester,as needed.5.2 Mechanical Sieve Shaker,conforming to Test MethodD1511.5.3 SievesU.S.Standard sieves or equivalents,conform-ing to Specification E11.Sieve Nos.12(1700-m)and 14(1400-m)shall be used.5.4 Bottom-Receiver Pan and Top-Sieve Cover.1This test meth
12、od is under the jurisdiction of ASTM Committee D24 on CarbonBlack and is the direct responsibility of Subcommittee D24.51 on Carbon BlackPellet Properties.Current edition approved June 1,2012.Published September 2012.Originallyapproved in 1974.Last previous edition approved in 2005 as D3313 05a.DOI:
13、10.1520/D3313-12.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The sole source of supply of the apparatus(the H
14、ITEC IPHT)known to thecommittee at this time is HITEC Luxembourg,5 rue de LEglise,L-1458,Luxembourg,E-mail:infohitec.lu,http:/www.hitec.lu/.(Some Model-S PelletStrength Testers with lab jack may still be in use and are suitable.This unit was inthe past available from A.L.Sweigart,Technical Service S
15、hop,1206 Hemlock St.,Borger,TX 79007.)If you are aware of alternative suppliers,please provide thisinformation to ASTM International Headquarters.Your comments will receivecareful consideration at a meeting of the responsible technical committee,1whichyou may attend.Copyright ASTM International,100
16、Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 5.5 Container,shallow,flat approximately 305 mm(12 in.)long.5.6 Forceps,fitted with sponge tips.A very low-densityurethane foam sponge has been found to be acceptable.6.Sampling6.1 Samples shall be taken in accordance with PracticesD1799 or D1900.7.Calibration7.1 Equipment used for this test shall be calibrated by deadweights or a force-measuring device that will verify theaccuracy of the equipment over the range to be