1、Designation:D343399(Reapproved 2020)Standard Test Method forFracture Strength in Cleavage of Adhesives in Bonded MetalJoints1This standard is issued under the fixed designation D3433;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,th
2、e year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method(1,2,3,4,5)2covers the determinationof fracture strength in cleavage of adhesives when tested ons
3、tandard specimens and under specified conditions of prepara-tion and testing(Note 1).1.2 This test method is useful in that it can be used todevelop design parameters for bonded assemblies.NOTE1While this test method is intended for use in metal-to-metalapplications it may be used for measuring frac
4、ture properties of adhesivesusing plastic adherends,provided consideration is given to the thicknessand rigidity of the plastic adherends.1.3 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.4 This standard does not purport to
5、address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.5 This international standard was develo
6、ped in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents
7、2.1 ASTM Standards:3A167 Specification for Stainless and Heat-ResistingChromium-Nickel Steel Plate,Sheet,and Strip(With-drawn 2014)4A366/A366M Specification for Commercial Steel(CS)Sheet,Carbon,(0.15 Maximum Percent)Cold-Rolled(Withdrawn 2000)4B36/B36M Specification for Brass Plate,Sheet,Strip,AndRo
8、lled BarB152/B152M Specification for Copper Sheet,Strip,Plate,and Rolled BarB209 Specification for Aluminum and Aluminum-AlloySheet and PlateB265 Specification for Titanium and Titanium Alloy Strip,Sheet,and PlateD907 Terminology of AdhesivesE4 Practices for Force Verification of Testing MachinesE39
9、9 Test Method for Linear-Elastic Plane-Strain FractureToughness KIcof Metallic Materials3.Terminology3.1 Definitions:Many of the terms used in this test methodare defined in Terminology D907.3.2 Definitions of Terms Specific to This Standard:3.2.1 crack-extension force,Gthe system isolated(fixedload
10、-displacement)loss of stress field energy for an infinitesi-mal increase,d A,of separational area.In equation form,GdA 5 2dUT(1)where UT=total elastic energy in the system(component ortest specimen).In the test specimens of this method,the crackfront is nearly straight through the specimen thickness
11、,B,sothat dA=B da,where da is an infinitesimal forward motion ofthe leading edge of the crack.Completely linear-elastic behav-ior is assumed in the calculations(see Annex A1)of G used inthis method,an allowable assumption when the zone ofnonlinear deformation in the adhesive is small relative tospec
12、imen dimensions and crack size.1This test method is under the jurisdiction of ASTM Committee D14 onAdhesives and is the direct responsibility of Subcommittee D14.80 on MetalBonding Adhesives.Current edition approved Jan.1,2020.Published January 2020.Originallyapproved in 1975.Last previous edition a
13、pproved in 2012 as D3433 99(2012).DOI:10.1520/D3433-99R20.2The boldface numbers in parentheses refer to the references at the end of thistest method.3For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards
14、volume information,refer to the standards Document Summary page onthe ASTM website.4The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standa
15、rd was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.3.2.1.1 Whe
16、n the shear stress on the plane of crack andforward to its leading edge is zero,the stress state is termed“opening mode.”The symbol for an opening mode G is GIforplane-strain and G1when the connotation of plane-strain is notwanted.3.2.2 opening mode fracture toughness,G1cthe value of Gjust prior to onset of rapid fracturing when G is increasing withtime.3.2.3 opening mode crack arrest toughness,G1athe valueof G just after arrest of a run-arrest segment of crack extension.3.2.3.1 It is assumed th