1、Designation:D3410/D3410M16Standard Test Method forCompressive Properties of Polymer Matrix CompositeMaterials with Unsupported Gage Section by ShearLoading1This standard is issued under the fixed designation D3410/D3410M;the number immediately following the designation indicates theyear of original
2、adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1
3、.Scope1.1 This test method determines the in-plane compressiveproperties of polymer matrix composite materials reinforced byhigh-modulus fibers.The composite material forms are limitedto continuous-fiber or discontinuous-fiber reinforced compos-ites for which the elastic properties are specially ort
4、hotropicwith respect to the test direction.This test procedure introducesthe compressive force into the specimen through shear atwedge grip interfaces.This type of force transfer differs fromthe procedure in Test Method D695 where compressive force istransmitted into the specimen by end-loading,Test
5、 MethodD6641/D6641M where compressive force is transmitted bycombined shear and end loading,and Test Method D5467/D5467M where compressive force is transmitted by subjectinga honeycomb core sandwich beam with thin skins to four-pointbending.1.2 This test method is applicable to composites made fromu
6、nidirectional tape,wet-tow placement,textile(for example,fabric),short fibers,or similar product forms.Some productforms may require deviations from the test method.1.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.Within the text theinch-pounds un
7、its are shown in brackets.The values stated ineach system are not exact equivalents;therefore,each systemmust be used independently of the other.Combining valuesfrom the two systems may result in nonconformance with thestandard.NOTE1Additional procedures for determining compressive propertiesof resi
8、n-matrix composites may be found in Test Methods D695,D5467/D5467M,and D6641/D6641M.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and de
9、termine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2D695 Test Method for Compressive Properties of RigidPlasticsD792 Test Methods for Density and Specific Gravity(Rela-tive Density)of Plastics by DisplacementD883 Terminology Relating to Plastic
10、sD2584 Test Method for Ignition Loss of Cured ReinforcedResinsD2734 Test Methods for Void Content of Reinforced PlasticsD3171 Test Methods for Constituent Content of CompositeMaterialsD3878 Terminology for Composite MaterialsD5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium
11、 Conditioning of Polymer MatrixComposite MaterialsD5379/D5379M Test Method for Shear Properties of Com-posite Materials by the V-Notched Beam MethodD5467/D5467M Test Method for Compressive Properties ofUnidirectional Polymer Matrix Composite Materials Us-ing a Sandwich BeamD6641/D6641M Test Method f
12、or Compressive Properties ofPolymer Matrix Composite Materials Using a CombinedLoading Compression(CLC)Test FixtureE4 Practices for Force Verification of Testing MachinesE6 Terminology Relating to Methods of Mechanical TestingE83 Practice for Verification and Classification of Exten-someter SystemsE
13、111 Test Method for Youngs Modulus,Tangent Modulus,and Chord ModulusE122 Practice for Calculating Sample Size to Estimate,With1This specification is under the jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.04 onLamina and Laminate Test M
14、ethods.Current edition approved March 15,2016.Published March 2016.Originallyapproved in 1975.Last previous edition approved in 2008 as D3410/D3410M 03(2008).DOI:10.1520/D3410_D3410M-16.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.
15、org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 Specified Precision,the Average for a Characteristic of aLot or Proces
16、sE132 Test Method for Poissons Ratio at Room TemperatureE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE251 Test Methods for Performance Characteristics of Me-tallic Bonded Resistance Strain GagesE456 Terminology Relating to Quality and StatisticsE1237 Guide for Installing Bonded Resistance Strain GagesE1309 GuideforIdentificationofFiber-ReinforcedPolymer-Matrix Composite Materials in Databases(With-drawn 2015)3E1434 Guide for Recording Mechanical Test Data of Fiber-Rei