1、Designation:D370496(Reapproved 2012)Standard Test Method forWear Preventive Properties of Lubricating Greases Usingthe(Falex)Block on Ring Test Machine in OscillatingMotion1This standard is issued under the fixed designation D3704;the number immediately following the designation indicates the year o
2、foriginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the determination of wearproperties of lu
3、bricating greases by means of the Falexblock-on-ring friction and wear test machine.1.2 The values stated in SI units are to be regarded asstandard except where equipment is supplied using inch-poundunits and would then be regarded as standard.The metricequivalents of inch-pound units given in such
4、cases in the bodyof the standard may be approximate.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of re
5、gulatory limitations prior to use2.Referenced Documents2.1 ASTM Standards:2D1403 Test Methods for Cone Penetration of LubricatingGrease Using One-Quarter and One-Half Scale ConeEquipmentD2714 Test Method for Calibration and Operation of theFalex Block-on-Ring Friction and Wear Testing MachineG40 Ter
6、minology Relating to Wear and Erosion3.Terminology3.1 Definitions:3.1.1 coeffcient of friction,or f,nin tribology,thedimensionless ratio of the friction force(F)between twobodies to the normal force(N)pressing these two bodiestogether.or5F/N!(1)3.1.1.1 DiscussionA distinction is often made betweenst
7、atic coeffcient of friction and kinetic coeffcient of friction.G403.1.2 friction force,nthe resisting force tangential to theinterface between two bodies when,under the action of anexternal force,one body moves or tends to move relative to theother.G403.1.3 kinetic coeffcient of friction,nthe coeffi
8、cient offriction under conditions of macroscopic relative motion be-tween two bodies.G403.1.4 wear,ndamage to a solid surface,generally involv-ing progressive loss of material,due to relative motion betweenthat surface and a contacting substance or substances.G404.Summary of Test Method4.1 The teste
9、r is operated with a steel test ring oscillatingagainst a steel test block.Test speed,load,angle of oscillation,time and specimen surface finish and hardness can be varied tosimulate field conditions.4.2 The width of the wear scar,developed on the test blockfrom contact with the oscillating test rin
10、g,is measured.5.Significance and Use5.1 This test method is used to differentiate between greaseshaving high,medium,and low wear preventive propertiesusing oscillating motion.The user of this method shoulddetermine to his own satisfaction whether results of this testprocedure correlate with field pe
11、rformance or other bench testmachines.6.Apparatus6.1 Falex Block-on-Ring Test Machine with FrictionRecorder,3described in detail in Annex A1 and illustrated inFig.1.1This test method is under the jurisdiction of ASTM Committee D02 onPetroleum Products,Liquid Fuels,and Lubricants and is the direct re
12、sponsibility ofSubcommittee D02.L0.05 on Solid Lubricants.Current edition approved April 15,2012.Published April 2012.Originallyapproved in 1978.Last previous edition approved in 2006 as D370496(2012).DOI:10.1520/D3704-96R12.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontac
13、t ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The sole source of supply of the apparatus known to the committee at this timeis Falex Corp.,1020 Airpark Dr.,Sugar Grove,IL 60554.If you ar
14、e aware ofalternative suppliers,please provide this information to ASTM InternationalHeadquarters.Your comments will receive careful consideration at a meeting of theresponsible technical committee,1which you may attend.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken
15、,PA 19428-2959.United States1 6.2 Falex Oscillating Drive Accessory,3described in detailin A1.6 and illustrated in Fig.2.6.3 Microscope,low-power(50 to 60)having sufficientclearance under objective to accommodate the test block.Itshould be fitted with a filar micrometer so that scar width maybe meas
16、ured with accuracy of 60.01 mm.6.4 Timer,graduated in minutes and seconds.7.Reagents and Materials7.1 Test Rings,Falex Type S-10 or S-253SAE 4620carburize steel,having a hardness of 58 to 63 HRC.The testring has a width of 8.15 mm(0.321 in.),a diameter of 35 mm(1.3775 in.),and a maximum radial run out of 0.013 mm(0.0005 in.).The surface roughness of the S-10 ring shall be0.15 to 0.30 m(6 to 12 in.)rms.The surface roughness of theS-25 ring shall be 0.51 to 0.71 m(22 to 28 in.)rms.7.2 Test Blocks,