1、Designation:D417922Standard Test Method forSingle Pellet Crush Strength of Formed Catalysts andCatalyst Carriers1This standard is issued under the fixed designation D4179;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of la
2、st revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers determining the resistance offormed catalysts and catalyst carriers to compressive force andis applic
3、able to regular catalyst shapes such as tablets andspheres.Other formed catalysts and catalyst carriersextrudates,granular materials,and other irregular shapes arespecifically excluded.1.2 This test method determines the average crush strengthin the range from 0 to 50 lbf(0 to 220 N).Some materials
4、mayhave crush strengths above 50 lbf(220N);the test method isapplicable to these materials,but the precision of the test is notknown.1.3 UnitsThe values stated in inch-pound units are to beregarded as standard.The values given in parentheses aremathematical conversions to SI units that are provided
5、forinformation only and are not considered standard.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the appli
6、cability of regulatory limitations prior to use.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by th
7、e World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2E105 Guide for Probability Sampling of MaterialsE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE456 Terminology Relating to Quality and StatisticsE691 Practice for
8、Conducting an Interlaboratory Study toDetermine the Precision of a Test Method3.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 pellets,nany catalyst shapetablets,spheres,orother similar configurationthat is not otherwise excludedfrom the scope of this test method.3.1.2 tablets,n
9、tableted cylindrical catalyst particles,ei-ther solid or hollow core,with lengths that do not vary from themean by more than 610%.4.Summary of Test Method4.1 Individual pellets taken from a representative sample areplaced between two flat surfaces,subjected to a compressiveload,and the force require
10、d to crush the pellet is measured.Theprocedure is replicated and the average of all measurementstaken is determined.5.Significance and Use5.1 This test method is intended to provide informationconcerning the ability of a catalyst shape to retain physicalintegrity during use.6.Apparatus6.1 A suitable
11、 compression testing device is required,con-sisting of the following:6.1.1 Calibrated Gauge,marked for direct reading of theforce in pounds(newtons).Additionally,a suitable system(mechanical,hydraulic,or pneumatic)must be provided so thatthe rate of force application is both uniform and controllable
12、within specified limits.6.1.2 Tool Steel Anvils,between which the sample will becrushed.The faces of the tool steel anvils shall be smooth andfree from recesses or ridges that would interfere with uniformcontact along the major axis of the pellet.When testing tabletsor spheres,the anvils may be of a
13、ny convenient size or shapeas long as their length and width are greater than the corre-sponding dimensions of the tablet or pellet being tested(seeFig.1).1This test method is under the jurisdiction of ASTM Committee D32 onCatalysts and is the direct responsibility of Subcommittee D32.02 on Physical
14、-Mechanical Properties.Current edition approved Aug.1,2022.Published August 2022.Originallyapproved in 1982.Last previous edition approved in 2017 as D4179 11(2017).DOI:10.1520/D4179-22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.
15、org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internation
16、ally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.17.Sampling7.1 A test sample of 50 to 200 individual pieces shall beobtained from larger composites by riffling or splitting inaccordance with subsection 5.12 of STP447A,3with the aim ofobtaining a representative sample that represents shape andsize distribu