1、Designation:D258313aStandard Test Method forIndentation Hardness of Rigid Plastics by Means of a BarcolImpressor1This standard is issued under the fixed designation D2583;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of la
2、st revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope*1.1 This test method covers the determinati
3、on of indentationhardness of both reinforced and nonreinforced rigid plasticsusing a Barcol Impressor,Model No.934-1 and Model No.935.1.2 The values stated in SI units are to be regarded asstandard.The values given in parentheses are for informationonly.1.3 This standard does not purport to address
4、all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.NOTE1There is no known ISO equivalent to this test method.2.Refe
5、renced Documents2.1 ASTM Standards:2D618 Practice for Conditioning Plastics for TestingD883 Terminology Relating to PlasticsD4000 Classification System for Specifying Plastic Materi-alsE691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method3.Terminology3.1 De
6、finitionsFor definitions of technical terms pertain-ing to plastics used in this test method,see Terminology D883.4.Summary of Test Method4.1 A materials surface hardness is determined through theuse of a Barcol Impressor.The relative depth of penetration ofthe Impressors indentor provides a compara
7、tive measure ofthe materials hardness.The Model No.934-1 and Model No.935 Barcol Impressors are designated for use with plastics.Within the range of hardness measured by these Impressors theModel No.934-1 is used for measuring harder materials andthe Model No.935 is used for measuring softer materia
8、ls.5.Significance and Use5.1 The Barcol Impressor is portable and therefore suitablefor testing the hardness of fabricated parts and individual testspecimens for production control purposes.5.2 Before proceeding with this test method,reference shallbe made to the specification of the material being
9、tested.Table1 of Classification System D4000 lists the ASTM materialstandards that currently exist.Any test specimen preparation,conditioning,dimensions,or testing parameters or combinationthereof covered in the relevant ASTM material specificationshall take precedence over those mentioned in this t
10、est method.If there are no relevant ASTM material specifications,then thedefault conditions apply.6.Apparatus(Fig.1 and Fig.2)6.1 Indentor3The indentor shall consist of a hardenedsteel truncated cone having an angle of 26 with a flat tip of0.157 mm(0.0062 in.)in diameter.It shall fit into a hollowsp
11、indle and be held down by a spring-loaded plunger.See Fig.2.6.2 Indicating DeviceThe indicating dial shall have 100divisions,each representing a depth of 0.0076-mm(0.0003-in.)penetration.The higher the reading is,the harder the materialis.6.3 Calibration Standards“Hard”and“soft”aluminumalloy disks s
12、upplied by the manufacturer of the instrument.Other disks should not be used,even if they are of the same1This test method is under the jurisdiction of ASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.10 on Mechanical Properties.Current edition approved Sept.1,2013.
13、Published September 2013.Originallyapproved in 1967.Last previous edition approved in 2013 as D2583-13.DOI:10.1520/D2583-13A.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer
14、 to the standards Document Summary page onthe ASTM website.3The sole source of supply of the apparatus known to the committee at this timeis Eurotherm/Barber-Colman,741F Miller Drive,Leesburg,VA 201758993.Ifyou are aware of alternative suppliers,please provide this information to ASTMInternational H
15、eadquarters.Your comments will receive careful consideration at ameeting of the responsible technical committee,1which you may attend.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United
16、 States1 alloy and temper as the manufacturers disks,as the hardnessof aluminum varies within any given alloy-temper parameter.6.4 A smooth glass plate is also needed.7.Test Specimens7.1 The testing area shall be smooth and free from mechani-cal defects.7.2 DimensionsTest specimens shall be at least 1.5 mm(116in.)thick and large enough to ensure a minimum distanceof 3 mm(18in.)in any direction from the indentor point to theedge of the specimen,as well as from test point to test point.8.Preparati