1、Designation:D245215(Reapproved 2019)Standard Test Method forExtrudability of Oil-and Resin-Base Caulking Compounds1This standard is issued under the fixed designation D2452;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of
2、last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method describes the laboratory procedure fordetermining the rate of extrusion of oil-and resin-base caulk-ing co
3、mpounds.1.2 The values stated in metric(SI)units are to be regardedas the standard.The values given in parentheses are providedfor information only.1.3 The subcommittee with jurisdiction is not aware of anysimilar ISO standard.1.4 This standard does not purport to address all of thesafety concerns,i
4、f any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accor-dance with internation
5、ally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2C717 Terminolog
6、y of Building Seals and SealantsD1475 Test Method for Density of Liquid Coatings,Inks,and Related Products3.Terminology3.1 DefinitionsDefinitions of the following terms arefound in Terminology C717:caulking compound,compound,sealant,standard conditions.4.Significance and Use4.1 The rate of extrusion
7、 determined by this test may becorrelated with the rate of gunning of the compound.5.Apparatus5.1 Press-Flow Extrusion Rheometer constructed in accor-dance with Fig.1.5.2 Air Supply and Pressure Gage,accurate to 6.9 kPa(1psi).5.3 Clamps and Stand to hold rheometer.5.4 Balance,accurate to 0.01 g.5.5
8、Stopwatch.5.6 Spatula(Steel).5.7 Weight-per-gallon Cup,capacity 83.2 cm3.6.Reagent6.1 Solvent,such as methyl ethyl ketone.7.Sampling7.1 The compound to be tested shall be taken from apreviously unopened container and thoroughly mixed beforeusing.8.Conditioning8.1 After thoroughly cleaning the press-
9、flow rheometer withsolvent,condition the compound and the rheometer in thelaboratory for at least 5 h at standard conditions.9.Procedure9.1 Remove the orifice holder from the rheometer cylinderand hold the open end up,making sure that the follower plateremains inside.9.2 Fill the cylinder with compo
10、und,avoiding air pockets.Strike off the filled cylinder with a spatula and replace thebottom orifice cap.Connect the tube to an air supply and fix itto a support stand above the balance.9.3 Adjust the air pressure to 207 kPa(30 psi)and open theair valve.If the pressure drops,readjust to 207 kPa whil
11、eextrusion is in progress.Close the air valve and discard thisextruded compound.The apparatus is now ready for testing.1This test method is under the jurisdiction ofASTM Committee C24 on BuildingSeals and Sealants and is the direct responsibility of Subcommittee C24.20 onGeneral Test Methods.Current
12、 edition approved Oct.1,2019.Published October 2019.Originallyapproved in 1966.Last previous edition approved in 2015 as D2452 15.DOI:10.1520/D2452-15R19.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStand
13、ards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on st
14、andardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 FIG.1 Press-Flow Extrusion RheometerD2452 15(2019)2 9.4 Open the air valve and start the
15、 stopwatch simultane-ously.After extruding approximately 50 g of compound,closethe air valve and stop the stopwatch simultaneously.Weigh tothe nearest 0.01 g the amount of compound extruded.9.5 Calculate the seconds per gram by dividing the numberof seconds elapsed by the number of grams extruded,an
16、ddesignate this as value S.9.6 Convert the value S to seconds per millilitre afterdetermining the specific gravity of the compound using theweight-per-gallon cup and Test Method D1475.NOTE1Since different compounds have different specific gravities,and the extrusion rate in terms of volume normally is of greater interestthan in terms of weight,the results shall be converted to terms of secondsper millilitre.10.Specific Gravity10.1 Weigh the weight-per-gallon cup accurately to 0.1 g.10.2 Remove t