1、Designation:D331402(Reapproved 2021)Standard Test Method forRubberChemical Analysis for Polystyrene Blocks In SBR(Styrene-Butadiene Rubber)and Styrene-ReinforcedLatices1This standard is issued under the fixed designation D3314;the number immediately following the designation indicates the year ofori
2、ginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the determination of longpolystyrene blocks i
3、n SBR rubbers and styrene-reinforcedlatices.1.2 Percent block styrene content may be determined in therange from 1 to 100%.1.3 This test method is intended for use on gel-freepolymers,but it may be used on polymers containing gel,if ithas been proven that gel does not interfere.1.4 This standard doe
4、s not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.For specific hazard state
5、ments,see Section 7.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization T
6、echnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D1076 Specification for RubberConcentrated,AmmoniaStabilized,Creamed,and Centrifuged Natural LatexD1416 Test Methods for Rubber from Synthetic SourcesChemical Analysis(Withdrawn 1996)3D4483 Practice for Evaluating Prec
7、ision for Test MethodStandards in the Rubber and Carbon Black ManufacturingIndustriesE145 Specification for Gravity-Convection and Forced-Ventilation Ovens3.Summary of Test Method3.1 The test method is based upon oxidative cleavage of theethylenic bonds in the block copolymer by treating a 1,2-dichl
8、orobenzene solution of the polymer with tertiary butylhydroperoxide(2-methyl-2-hydroperoxypropane)with os-mium tetroxide catalyst.The saturated portions of the polymer,which contain no ethylenic bonds,remain unattacked.Thesmall fragments(low molecular weight aldehydes)and thelow-molecular weight pol
9、ystyrene fragments from scissionswithin the random copolymer block are soluble in methylalcohol,whereas the detached high-molecular weight polysty-rene from the styrene homopolymer block is insoluble inalcohol.It is therefore possible to separate the high-molecularweight polystyrene,which constitute
10、s the homopolymer block,from the polymer solution.4.Significance and Use4.1 This test method is suitable for manufacturing control,development,and research studies.5.Apparatus5.1 Erlenmeyer Flask,or round-bottom flask for use withthe heating mantle,of 250-cm3capacity with ground-glassjoint.An iodine
11、 flask is also satisfactory.5.2 Air Condenser,for 5.1.5.3 Beaker,600-cm3.5.4 Graduated Cylinder,50-cm3.5.5 Pipet,1-cm3.5.6 Buret,100-cm3,for dispensing tertiary butyl hydroper-oxide.5.7 Thermometer,to 150C range.5.8 Crucible,Gooch-type,fritted-glass,medium-porosity,25 to 50-cm3size.1This test method
12、 is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct responsibility of Subcommittee D11.11on Chemical Analysis.Current edition approved Nov.1,2021.Published December 2021.Originallyapproved in 1974.Last previous edition approved in 2017 as D3314 02(20
13、17).DOI:10.1520/D3314-02R212For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved version of this hist
14、orical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision o
15、n Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1?5.9 Hot Plate,capable of operating to provide 120 to 130Cto boiling solution,or heating mantle for round-bottom flasksoperating in
16、the same temperature range.5.10 Drying Oven,capable of controlling at 100C Type 1Boven in accordance with Specification E145.6.Reagents6.1 Purity of ReagentsReagent grade chemicals shall beused in all tests.Unless otherwise indicated,it is intended thatall reagents shall conform to the specifications of the Commit-tee on Analytical Reagents of the American Chemical Society,where such specifications are available.4Other grades may beused,provided it is first ascertained that the reagent is ofsuff