1、Designation:D333617Standard Test Method forLife of Lubricating Greases in Ball Bearings at ElevatedTemperatures1This standard is issued under the fixed designation D3336;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of las
2、t revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope*1.1 This test method covers the evaluation o
3、f the perfor-mance of lubricating greases in ball bearings operating underlight loads at high speeds and elevated temperatures.1.2 The values stated in SI units are to be regarded asstandard.1.2.1 ExceptionThe values given in parentheses are math-ematical conversions to inch-pound units that are pro
4、vided forinformation only and are not considered standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility
5、 of regulatory limitations prior to use.For specificwarning statements,see 8.1.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides an
6、d Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2A600 Specification for Tool Steel High Speed2.2 ABMA Standard:3Standard 4,Tolerance Definitions and Gaging Practices forBall and Roller Bearings3.Summary of Te
7、st Method3.1 A grease lubricated SAE No.204 size ball bearing isrotated at 10 000 r/min under light load at a specified elevatedtemperature.Tests are continued until failure or completion ofa specified number of hours of running time.4.Significance and Use4.1 This test method can be used to evaluate
8、 the ability ofgrease to provide adequate lubrication for extended periods ofball bearings operating under light loads at high speeds andelevated temperatures.5.Apparatus4,55.1 Test Spindle6(see Figs.1-4),capable of operating atspeeds of 10 000 r min and temperatures as high as 371 C(700 F).The test
9、 bearing seat dimension shall be 19.99 mm to20.00 mm(0.7870 in.to 0.7874 in.).For spindles having thetest bearing and the support bearing in the same housing(CRCType,Figs.1-3)(Note 2)the internal construction of thespindle shall be such that the outboard support bearing,or bothbearings are free to f
10、loat axially in the housing.In designswhere both bearings are free to float,the spindle shaft shallhave a 0.508 mm to 0.762 mm(0.020 in.to 0.030 in.)free axialmovement or end play.The outboard bearing seat dimensionshould be 19.99 mm to 20.00 mm(0.7870 in.to 0.7874 in.).5.1.1 The test unit design(Fi
11、g.1 and Fig.2)should be suchthat a finger spring washer produces a 22 N to 67 N(5 lbf to15 lbf)thrust load on the floating outboard support bearing.7,55.2 Bearing Housing:1This test method is under the jurisdiction of ASTM Committee D02 onPetroleum Products,Liquid Fuels,and Lubricants and is the dir
12、ect responsibility ofSubcommittee D02.G0.05 on Functional Tests-Temperature.Current edition approved June 1,2017.Published June 2017.Originallyapproved in 1975.Last previous edition approved in 2015 as D3336 05(2015).DOI:10.1520/D3336-17.2For referenced ASTM standards,visit the ASTM website,www.astm
13、.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Available from American Bearing Manufacturers Assoc.,2025 M St.,NW,Ste800,Washington,DC 20036.4Complete apparatus is available
14、from Falex Corp.,1020 Airpark Dr.,SugarGrove,IL 60554.5If you are aware of alternative suppliers,please provide this information toASTM International Headquarters.Your comments will receive careful consider-ation at a meeting of the responsible technical committee,1which you may attend.6Pope Machine
15、ry Corporation Grease Test Spindles No.P-1911 or P-6301A-HT(Fig.1)and No.P-7605-B(Fig.2);and Falex Corp.spindles of the type shown inFig.1 and Fig.2 have been found satisfactory for this purpose.7The sole source of supply of the apparatus known to the committee at this timeis Falex Part No.643-187-0
16、70,Falex Corp.1020 Airpark Dr.,Sugar Grove,IL60554.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Tech