1、Designation:D434010Standard Test Method forCorrosion of Cast Aluminum Alloys in Engine CoolantsUnder Heat-Rejecting Conditions1This standard is issued under the fixed designation D4340;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,
2、the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers a laboratory screening proce-dure for evaluating the effectiveness of engine coolants i
3、ncombating corrosion of aluminum casting alloys under heat-transfer conditions that may be present in aluminum cylinderhead engines.1.2 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish
4、 appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.Specific precau-tionary statements are given in Sections 11 and 12.2.Referenced Documents2.1 ASTM Standards:2D1176 Practice for Sampling and Preparing Aqueous Solu-tions of Engine Coolan
5、ts orAntirusts for Testing Purposes3.Summary of Test Method3.1 In this test method,a heat flux is established through acast aluminum alloy typical of that used for engine cylinderheads while exposed to an engine coolant under a pressure of193 kPa(28 psi).The temperature of the aluminum specimenis ma
6、intained at 135C(275F)and the test is continued for 1week(168 h).The effectiveness of the coolant for preventingcorrosion of the aluminum under heat-transfer conditions(hereafter referred to as heat-transfer corrosion)is evaluated onthe basis of the weight change of the test specimen.4.Significance
7、and Use4.1 It is essential that engine coolants prevent heat-transfercorrosion of aluminum cylinder heads during engine operation.Any corrosion products formed may deposit on interior radia-tor surfaces,reducing heat-transfer efficiency of the radiator.Overheating and boil-over of the cooling system
8、 may thenoccur.4.2 This test method provides a means for selectivelyscreening unused engine coolants and will readily distinguishthose coolants that are unsuitable for use with aluminumcylinder head engines.However,satisfactory performance of acoolant in this test method does not ensure adequate lon
9、g-termservice performance.Additional,more comprehensive evalua-tions with simulated service,dynamometer,and vehicle testsshould be used to establish the long-term effectiveness of thecoolant.5.Apparatus5.1 Heat-Transfer Corrosion CellThe assembled corro-sion cell is shown schematically in Fig.1.It i
10、s assembled fromcomponents,some of which require glass blowing or machin-ing.The glass O-ring cell shall be constructed from two glassO-ring joints3joined to an additional middle section of glasstubing4of the same diameter to make a total length of 53 cm(21 in.).Heat-resistant O-rings5shall be used.
11、Internal pressureshall be monitored using a suitable pressure gage,6and apressure-relief valve7shall be installed to protect againstbursting.5.1.1 The top assembly plate(shown in Fig.2)shall beconstructed of stainless steel,and the heat-transfer bar andbottom assembly plate(also illustrated in Fig.2
12、)shall prefer-ably be constructed of stainless steel.Mild steel may be usedfor the heat-transfer bar and bottom assembly plate.1This test method is under the jurisdiction of ASTM Committee D15 on EngineCoolants and is the direct responsibility of Subcommittee D15.06 on GlasswarePerformance Tests.Cur
13、rent edition approved Dec.1,2010.Published January 2011.Last previousedition approved in 2007 as D4340 96(2007).DOI:10.1520/D4340-10.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume informati
14、on,refer to the standards Document Summary page onthe ASTM website.3Corning 6780,No.40 Pyrex Brand O-ring joints have been found satisfactory.Equivalent O-ring joints with a low coefficient of expansion may be used.4Pyrex Brand Glass,a trademark of Corning Glass Works,with a standard wallthickness o
15、f 2.0 mm has been found satisfactory.Equivalent high-strength glass witha low coefficient of expansion may be used.5Viton,a trademark of E.I.duPont de Nemours and Co.,Inc.has been foundsatisfactory.Silicone O-rings may also be satisfactory.Polytetrafluoroethylene is notsuitable due to a high creep r
16、ate at the test temperature.6Ametek,U.S.Gauge Division,Model E-82 has been found satisfactory.Anequivalent pressure gage may be used.7Nupro,Catalog No.SS-4CPA2-3 has been found satisfactory.An equivalentpressure relief valve may be used.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 5.2 Temperature Controller,8with high-temperature alarmoption and temperature control range up to at least 150C(302F).Use Type J thermocouple.A heavy-dut