1、Designation:D117115Standard Test Method forRubber DeteriorationSurface Ozone Cracking Outdoors orChamber(Triangular Specimens)1This standard is issued under the fixed designation D1171;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,
2、the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method permits t
3、he estimation of the relativeability of rubber compounds used for applications requiringresistance to outdoor weathering.1.2 This test method is not applicable to materials ordinarilyclassed as hard rubber,but is adaptable to molded or extrudedsoft rubber materials and sponge rubber for use in windo
4、wweatherstripping as well as similar automotive applications.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bil
5、ity of regulatory limitations prior to use.For a specifichazard statement,see Note 1 and 8.1.NOTE1WarningOzone is a hazardous chemical.2.Referenced Documents2.1 ASTM Standards:2D518 Test Method for Rubber DeteriorationSurfaceCracking(Withdrawn 2007)3NOTE2The procedures in Test Method D518 have been
6、incorporatedas Procedures B1,B2,and B3 in Test Methods D1149.D1149 Test Methods for Rubber DeteriorationCracking inan Ozone Controlled EnvironmentD4575 Test Methods for Rubber DeteriorationReferenceand Alternative Method(s)for Determining Ozone Levelin Laboratory Test Chambers3.Summary of Test Metho
7、d3.1 Procedures are given for preparing triangular cross-section specimens,for mounting them in strained conditionaround specified circular mandrels,and for rating the effect ofexposure as evidenced by the appearance of surface cracks.The type,time,temperature,and other conditions of exposureare not
8、 given but shall be agreed upon by the purchaser and theseller and shall be completely described in the test reports.3.2 Two techniques are described,the exposure rating andthe quality-retention rating.4.Significance and Use4.1 Molded or extruded rubber products must withstand theeffects of ozone cr
9、acking and outdoor weathering for satisfac-tory use.This test enables a simple comparison of performanceto be made under specified test conditions in an outdoor test.No direct correlation between test performance and serviceperformance can be claimed due to the wide range of serviceconditions.5.Appa
10、ratus5.1 Mounting MandrelA wood mandrel 50 mm(2 in.)inoutside diameter,suitably coated with spar varnish or a clearlacquer.The mandrel may be supported by any convenientmethod.5.2 Fastening Wire Enameled copper wire.6.Test Specimen6.1 The triangular cross-section test specimen shall be amolded,extru
11、ded,or sponge section with a continuous skin orsurface layer,250 mm(10 in.)long,and cured in a straightposition.The cross-sectional dimensions shall be as shown inFig.1.Duplicate specimens shall be tested.6.2 It is recommended that the manufacturer observe aminimum rest period of 24 h between compou
12、nd mixing andcompound preparation,and a minimum rest period of12hbetween compound preparation and curing when preparingspecimens.The finish of the specimens shall be as smooth aspossible.METHOD AEXPOSURE RATING7.Procedure7.1 Mounting of SpecimensPlace bench marks on eachspecimen with a crayon,190 mm
13、(7.5 in.)apart and 32 mm1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand is the direct responsibility of Subcommittee D11.15 on Degradation Tests.Current edition approved July 1,2015.Published September 2015.Originallyapproved in 1951.Last previous edition approved in 2
14、007 as D1171 99(2007).DOI:10.1520/D1171-15.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved vers
15、ion of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1(1.25 in.)from the ends.Form the specimens into a loop byplacing the 19-mm(0.75-in.)sides together and tying securelywith wire at
16、the bench marks.Slip the complete loop over themandrel.Place as many specimens on the mandrels as length ofmandrel will permit.7.2 Exposure of Specimens:7.2.1 Conditioning Period:7.2.1.1 Outdoor ExposureAfter the specimens aremounted allow them to condition for 70 to 72 h at roomtemperature in an ozone free atmosphere.Do not touch thelooped part after mounting until the test is completed.7.2.2 Angle and Direction and Positioning of Exposures:7.2.2.1 Incline specimens exposed outdoors so that the