1、Designation:D217616Standard Test Method forFolding Endurance of Paper and Plastics Film by the M.I.T.Tester1This standard is issued under the fixed designation D2176;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last re
2、vision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope*1.1 This test method describes the use of the M.
3、I.T.-typefolding apparatus for determining folding endurance of paperand plastics film.The M.I.T.tester can be adjusted for samplesof any thickness;however,if the outer layers thicker than about0.25 mm(0.01 in.)rupture during the first few folds,the testloses its significance.The procedure for the S
4、chopper-typeapparatus is given in Test Method D643.1.2 The values stated in SI units are to be regarded asstandard.The values given in parentheses are mathematicalconversions to inch-pound units that are provided for informa-tion only and are not considered standard1.3 This standard does not purport
5、 to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2D585 Pract
6、ice for Sampling and Accepting a Single Lot ofPaper,Paperboard,Fiberboard,and Related Product(Withdrawn 2010)3D643 Test Method for Folding Endurance of Paper by theSchopper Tester(Withdrawn 2010)3D685 Practice for Conditioning Paper and Paper Productsfor TestingD1968 Terminology Relating to Paper an
7、d Paper ProductsE122 Practice for Calculating Sample Size to Estimate,WithSpecified Precision,the Average for a Characteristic of aLot or Process3.Terminology3.1 Definitions shall be in accordance with TerminologyD1968 and the Dictionary of Paper.44.Significance and Use4.1 The folding endurance is f
8、requently used to estimate theability of the paper and plastics film to withstand repeatedbending,folding,and creasing.4.2 Folding endurance has also been found useful in mea-suring the deterioration of paper and plastics film upon aging.5.Apparatus5.1 Folding Tester,consisting of:5.1.1 A spring-loa
9、ded clamping jaw constrained to movewithout rotation in a direction perpendicular to the axis ofrotation of the folding head specified below and having itsclamping surfaces in the plane of this axis.The load is appliedby a spring attached to the jaw assembly which is easilyadjustable to provide any
10、desired tension on the specimenwithin range of 4.9 to 14.72 N(500 to 1500 gf).The deflectionof the spring when loaded shall be at least 17 mm(0.67in.)/9.81 N,which is achieved by using a weight of 1 kg mass.5.1.2 An oscillating folding head supporting two smooth,cylindrical folding surfaces parallel
11、 to,and symmetricallyplaced with respect to,the axis of rotation.Each of the twofolding surfaces shall have a radius of curvature of 0.38 mm(0.015 6 0.001 in.)and a width of 19 mm(0.75 6 0.04 in).The distance separating the folding surfaces is greater than theuncompressed thickness of the specimen b
12、eing tested by nomore than 0.25 mm(0.010 in.).The position of the axis ofrotation is midway between the common tangent planes of thetwo folding surfaces.The folding head is provided with aclamping jaw with its nearest edge not less than 9.5 mm(0.3751This classification system is under the jurisdicti
13、on ofASTM Committee D20 onPlastics and is the direct responsibility of Subcommittee D20.15 on ThermoplasticMaterials.Current edition approved Nov.1,2016.Published November 2016.Originallyapproved in 1956.Last previous edition approved in 2007 as D2176-97a(2007),which was withdrawn May 2010 and reins
14、tated in November 2016.DOI:10.1520/D2176-16.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved ver
15、sion of this historical standard is referenced onwww.astm.org.4Available from Technological Association of the Pulp and Paper Industry(TAPPI),15 Technology Parkway South,Suite 115,Peachtree Corners,GA 30092,http:/www.tappi.org.*A Summary of Changes section appears at the end of this standardCopyrigh
16、t ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 in.)beyond the axis of rotation.The rotary oscillating move-ment of the head is such as to fold the specimen through anangle of 135 6 2,both to the right and to the left of theposition of the unfolded specimen.5.1.3 Various size folding heads are required for testingdifferent thicknesses of specimens.Heads available will ac-commodate thicknesses from 0 to 0.25 mm(0 to 0.01 in.),0.25to 0.50 mm(0.