1、Designation:D223017(Reapproved 2022)Standard Test Method forRubber PropertyExtrudability of UnvulcanizedCompounds1This standard is issued under the fixed designation D2230;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of l
2、ast revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the determination of the extrud-ability of unvulcanized SBR and NBR rubber compoundsthrough a screw-
3、type extruder equipped with ASTM ExtrusionDie,Garvey type.This test method is designed to allow theobservation of the appearance and contours of the extrusion.Rating systems are provided along with recipes for compoundsof known extrusion characteristics.The utility of the testmethod for evaluating r
4、ubbers or compounding materials otherthan those listed has not been established.Since extrusionmachines differ among laboratories,the procedure includestechniques that minimize differences between machines.1.2 The values stated in SI units are to be regarded as thestandard.The values given in parent
5、heses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory
6、 limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organiza
7、tion TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D3182 Practice for RubberMaterials,Equipment,and Pro-cedures for Mixing Standard Compounds and PreparingStandard Vulcanized SheetsD3185 Test Methods for RubberEvaluation of SBR(Styrene-Butadiene Rubber)Including
8、Mixtures With OilD3187 Test Methods for RubberEvaluation of NBR(Acrylonitrile-Butadiene Rubber)2.2 ASTM Adjuncts:Appearance Ratings Photographs33.Summary of Test Method3.1 A standard compound is prepared and extruded througha specially shaped die that produces an extrusion having acombination of rel
9、atively flat surfaces,sharp corners,and thinsections.The operating conditions are varied until a satisfac-tory extrusion of the standard compound is obtained.The testcompound is then extruded,using the conditions justestablished,and the nature of the extrusion is rated visually forsmoothness,sharp c
10、orners,and integrity of thin sections.4.Significance and Use4.1 One objective in the extrusion of rubber compounds isto obtain a smooth extrusion that closely reproduces thecontours of the extrusion die.This test method provides for asubjective determination of this under controlled conditions.As th
11、e rating is subjective,it does not lend itself readily toincorporation as a specification requirement.It does not mea-sure other aspects of extrudability such as rate of extrusion ordie swell in a quantitative manner.5.Apparatus5.1 Mill,150 mm by 300 mm(6 in.by 12 in.),as describedin Practice D3182.
12、5.2 DieASTM Extrusion Die,Garvey type,conforming tothe dimensions and shape shown in Fig.1 shall be used.NOTE1Good precision in the manufacture of the opening in the diecan be attained by ultrasonic machining.The die should be replaced whena dimension has changed by 0.02 mm(0.001 in.)from its origin
13、al valueor if the die is damaged.5.3 AdapterA hollow,cone-shaped ring insert taperedwith an angle of 30 6 15(shown in Fig.2)shall be used with1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct responsibility of Subcommittee D11.12on
14、 Processability Tests.Current edition approved Oct.1,2022.Published October 2022.Originallyapproved in 1963.Last previous edition approved in 2017 as D2230 171.DOI:10.1520/D2230-17R22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.or
15、g.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Glossy prints of Figs.3 and 4 are available at a nominal cost from ASTMInternational Headquarters.OrderAdjunct No.ADJD2230-E-PDF.Original adjunctproduced in 1986.Copyright ASTM Inte
16、rnational,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1the die to contour the interior of the extruder head.This willreduce turbulent flow of the rubbe